Technical Library | 2015-05-14 15:45:45.0
The Printed Circuit Board industry has seen a steady reduction in pitch from 1.0mm to 0.4mm; a segment of the industry is even using or considering a 0.25mm pitch. This has increased the use of stacked microvias in these designs. The process of stacking microvias has been practiced for several years in handheld devices; however, the devices generally do not operate in harsh conditions. Type 1 and Type 2 microvias have been tested over the years and have been found to be very reliable. We do not have enough test data for 3 and 4 stack microvias when placed on and off buried via. The main objective of this study was to understand the reliability of 3 and 4 stack microvias placed on and off a buried via.
Technical Library | 2016-11-30 15:53:15.0
The use of microvias in Printed Circuit Boards (PCBs) for military hardware is increasing as technology drives us toward smaller pitches and denser circuitry. Along with the changes in technology, the industry has changed and captive manufacturing lines are few and far between. As PCBs get more complicated, the testing we perform to verify the material was manufactured to our requirements before they are used in an assembly needs to be reviewed to ensure that it is sufficient for the technology and meets industry needs to better screen for long-term reliability. The Interconnect Stress Testing (IST) protocol currently used to identify manufacturing issues in plated through holes, blind, or buried vias are not necessarily sufficient to identify problems with microvias. There is a need to review the current IST protocol to determine if it is adequate for finding bad microvias or if there is a more reliable test that will screen out manufacturing inconsistencies. The objective of this research is to analyze a large population of PCB IST coupons to determine if there is a more effective IST test to find less reliable microvias in electrically passing PCB product and to screen for manufacturing deficiencies. The proposed IST test procedure will be supported with visual inspection of corresponding microvia cross sections and Printed Wiring Assembly (PWA) acceptance test results. The proposed screening will be shown to only slightly affect PCB yield while showing a large benefit to screening before PCBs are used in an assembly.
Technical Library | 2021-01-21 02:04:27.0
Traditional single level microvia structures are generally considered the most robust type of interconnection within a printed wire board (PWB) substrate. The rapid implementation of HDI technology now commonly requires between 2, 3 or 4 levels of microvias sequentially processed into the product. Recent OEM funded reliability testing has confirmed that by increasing the levels (stack height) these structures are proving less reliable, when compared to their single or double level counterparts. Recently false positive results have been recorded on products tested with traditional thermal shock testing methodology (cycling between -40°C and 125°C, or 145°C). A number of companies are incurring product failures resulting in increased costs associated with replacing the circuit boards, components and added labour.
Technical Library | 2007-05-09 18:26:16.0
High Density Interconnect (HDI) technology is fast becoming the enabling technology for the next generation of small portable electronic communication devices. These methods employ many different dielectrics and via fabrication technologies. In this research, the effect of the proximity of microvias to Plated Through Holes (PTHs) and its effect on the reliability of the microvias was extensively evaluated. The reliability of microvia interconnect structures was evaluated using Liquid-To-Liquid Thermal Shock (LLTS) testing (-55oC to +125oC). Comprehensive failure analysis was performed on microvias fabricated using different via fabrication technologies.
Technical Library | 2009-04-30 18:06:24.0
This presentation surveys the most significant via and via-related laminate failure mechanisms from past to present using data from current induced thermal cycling (CITC) testing, failure analysis, and other sources. The relative life and failure modes of thru vias, buried vias, and microvias (stacked vs. non-stacked) are compared, along with the affect of structure, materials, and peak temperatures on the above. The origin of via-induced laminate failures such as "eyebrow cracks" and Pb free related internal delamination is also explored.
Technical Library | 2007-06-06 15:25:30.0
Though today's microvias and high aspect plated through holes (PTH's) look nothing like the earliest through holes of 40 years ago, the PTH in its various forms remains the “weak link” and most critical element of printed wiring boards and laminate chip carriers (...) The paper outlines an approach to evaluating PTH reliability and quality that involves characterizing PTH life across a range of temperatures to reveal intricacies not seen by testing at a single delta-T, and certainly difficult to predict by modeling alone.
Technical Library | 2013-09-19 17:25:32.0
The next generation of smart phones will demand very thin multi-layer boards to reduce the product thickness again. This paper shows three different manufacturing approaches, which can be used for very thin any-layer build-ups. The technological approaches are compared on reliability level – the any-layer copper filled micro-via technology which is to be considered as state of the art technology for high end phones and the ALIVH-C/G technology that is well established in Japan. A test vehicle design featuring test coupons for comprehensive reliability test series has been defined as target application for investigation...
Technical Library | 2020-07-22 19:39:05.0
The PWB industry needs to complete reliability testing in order to define the minimum copper wrap plating thickness requirement for confirming the reliability of PTH structures. Predicting reliability must ensure that the failure mechanism is demonstrated as a wear-out failure mode because a plating wrap failure is unpredictable. The purpose of this study was to quantify the effects of various copper wrap plating thicknesses through IST testing followed by micro sectioning to determine the failure mechanism and identify the minimum copper wrap thickness required for a reliable PWB. Minimum copper wrap plating thickness has become an even a bigger concern since designers started designing HDI products with buried vias, microvias and through filled vias all in one design. PWBs go through multiple plating cycles requiring planarization after each plating cycle to keep the surface copper to a manageable thickness for etching. The companies started a project to study the relationship between Copper wrap plating thickness and via reliability. The project had two phases. This paper will present findings from both Phase 1 and Phase 2.