Technical Library | 2020-11-09 16:59:53.0
A customer contacted ACI Technologies regarding a high failure rate of their assemblies. They provided assemblies to be X-rayed and inspected for the purpose of identifying any process related issues such as (but not limited to) solder and assembly workmanship and evidence of damage due to moisture related problems during reflow (a.k.a. "popcorning"). Moisture damage usually appears as physical damage to the component. The first indication of moisture damage would be externally observable changes to the package in the form of bulging or fractures to the outer surface of the component, an example of which is shown in Figure 1. Internally observable indicators of moisture damage typically include fractures to the die inside the package and lifted or fractured wire bonds. These conditions would be apparent during transmissive X-ray inspection. Another symptom of moisture related damage would be inconsistent solder joint sizes that result from package deformation during the liquidus phase of the reflow process. None of these indicators of moisture related damage were present on the customer samples.
Technical Library | 2021-02-20 00:55:47.0
Customers must be able to rely on accurate humidity indication as an assurance of SMD quality and fitness for processing and use. Without it, they might accept SMDs from suppliers that have already been irreparably damaged by moisture during storage or transit. Or, they might approve for processing SMDs that have been improperly or insufficiently heat-dried. Beyond the processing questions, there are financial questions: Where did the dry pack problems originate and who--supplier, customer, shipper--is financially responsible for the damaged SMDs? In response, Clariant, the originator of the color change humidity indicator card, and a member of the JEDEC's Subcommittee 14.1, "Reliability and Test Methods for Packaged Devices," created a new "non-reversible" halogen and cobalt dichloride free humidity indicator card. This HIC combines two reversible indicators (5% and 10%) with a new non-reversible (60% RH) indicator spot. (Figure 1) The 5% and 10% reversible spots work the way similar indicators do: they change color from blue (dry), to lavender, to pink (wet) to indicate humidity exposure at the indicated levels. If humidity levels drop, they will gradually revert back to blue.
Technical Library | 1999-05-06 10:46:06.0
Pentium-class portables present significant packaging problems. The heat generated inside a notebook not only reduces microprocessor reliability, but the reliability of peripheries such as hard drives and video chips. Although the processor is the primary heat-generating source, it isn’t always the component least tolerant of temperature...
Technical Library | 2022-12-23 20:44:54.0
One of the upcoming reliability issues which is related to the lead-free solder introduction, are the headin-pillow solderability problems, mainly for BGA packages. These problems are due to excessive package warpage at reflow temperature. Both convex and concave warpage at reflow temperature can lead to the head-in-pillow problem where the solder paste and solder ball are in mechanical contact but not forming one uniform joint. With the thermo-Moiré profile measurements, this paper explains for two flex BGA packages the head-in-pillow. Both local and global height differences higher than 100 µm have been measured at solder reflow temperature. This can be sufficient to have no contact between the molten solder ball and solder paste. Finally, the impact of package drying is measured
Technical Library | 1999-05-06 11:52:21.0
The market's demand for increasingly powerful products, in smaller and smaller packaging, creates a cooling problem. Integrated circuit (IC) lifetime is dependent upon its operating temperature, creating a trade-off situation: either you enlarge the package to accept additional cooling, or you sacrifice IC lifetime.
Technical Library | 2009-03-13 00:27:09.0
Open product reliability testing in Stockholm, Sweden in January as part of a live production event generated some quite startling results. It was apparent that many components simply cannot handle the high reflow temperatures of a lead-free soldering process, and that many surface-mount machine suppliers are battling significant problems with QFN packages and other components that are mounting edgeways (bill boarding). However, some suppliers have achieved good results.
Technical Library | 2019-04-30 08:04:19.0
Every industry has every unwritten rules, like IC shipping tube moq is high in packaging tube industry rules! This regulation is not to be difficult for customers, but the cost of the problem, as long as the manufacturers feel that even a small amount of packaging tube can do and do too.
Technical Library | 2006-06-29 13:37:36.0
Electronic Packaging is a critical part of all electronic devices and can be a source of the reliability problems experienced by systems using those devices. In many cases, the packaging defects are intermittent in nature and difficult to detect. This paper describes a tester that has been used for 20 years on commercial products and has proven to be extremely effective in detecting these defects prior to component assembly.
Technical Library | 2013-01-17 15:37:21.0
A problem exists with electroless nickel / immersion gold (ENIG) surface finish on some pads, on some boards, that causes the solder joint to separate from the nickel surface, causing an open. The solder has wet and dissolved the gold. A weak tin to nickel intermetallic bond initially occurs, but the intermetallic bond cracks and separates when put under stress. Since the electroless nickel / immersion gold finish performs satisfactory in most applications, there had to be some area within the current chemistry process window that was satisfactory. The problem has been described as a 'BGA Black Pad Problem' or by HP as an 'Interfacial Fracture of BGA Packages…'[1]. A 24 variable experiment using three different chemistries was conducted during the ITRI (Interconnect Technology Research Institute) ENIG Project, Round 1, to investigate what process parameters of the chemical matrix were potentially satisfactory to use and which process parameters of the chemical matrix need to be avoided. The ITRI ENIG Project has completed Round 1 of testing and is now in the process of Round 2 TV (Test Vehicle) build.
Technical Library | 2019-02-06 22:02:08.0
The High Density Packaging (HDP) user group has completed a project to evaluate the majority of viable Dk (Dielectric Constant)/Df (Dissipation Factor) and delay/loss electrical test methods, with a focus on the methods used for speeds above 2 GHz. A comparison of test methods from 1 to 2 GHz through to higher test frequencies was desired, testing a variety of laminate materials (standard volume production with UL approval, low loss, and "halogen-free" laminate materials). Variations in the test board material resin content/construction and copper foil surface roughness/type were minimized. Problems with Dk/Df and loss test methods and discrepancies in results are identified, as well as possible correlations or relationships among these higher speed test methods.