Technical Library | 2019-05-24 09:22:59.0
There is a smaller process window and a much narrower margin of error when creating and using lead-free reflow profiles for surface mount parts on printed circuit boards (PCBs). Solder balls, dewetting, tombstones, voids, and head-on-pillow problems will occur much more frequently because lead-free alloys behave differently than eutectic pastes. Problems are compounded due to the extra heat necessary for some lead-free pastes to reach their melting points.
Technical Library | 2019-06-24 15:54:17.0
Defense systems and its manufacturers are often blamed for not embracing new and innovative technologies to manufacture products compared to its commercial counterparts. Commercial product manufacturers are known to think “outside the box” in coming up with new products which are cheaper, have fewer parts, and easier to manufacture using automation. Automation leads to consistent quality products which are reliable and reproducible. Implementing some of these producibility design practices into defense systems will greatly reduce the cost and insertion time for new products.
Technical Library | 2019-06-19 11:06:46.0
Tin (Sn) metal displays the characteristic of growing “tin whiskers” from pure tin coatings (most actively on relatively thin, electrodeposited or immersion tin coatings), usually months or years from the initial deposition of the tin. Tin whiskers are electrically conductive, filamentary, single crystals of white (beta phase) tin. These filaments of single crystal tin are usually one to five microns in diameter, and a few microns up to several tens of millimeters long, that grow spontaneously from the tin coatings. Alloying additions of several percent (by weight) of lead (Pb) prevents these electrically conductive tin whiskers from growing. Pb alloyed into the Sn was discovered to prevent the occurrence of tin whiskers in electronic assemblies in the 1950s as the Bell Laboratories solution to the problem of tin whiskers. The alloying of the tin with lead has thus quietly averted incalculable losses from short circuits in electronic equipment for the last 60 years.
Technical Library | 2020-03-09 10:50:17.0
A customer called the Helpline seeking advice for cleaning no-clean fluxes prior to applying a conformal coating. The customer's assemblies were manufactured with a no-clean rosin based solder paste (ROL0) and were cleaned with an isopropyl alcohol (IPA) wash. After cleaning, a white residue was sometimes found in areas with high paste concentrations and was interfering with the adhesion of the conformal coating (Figure 1). For conformal coatings to adhere properly, the printed circuit board (PCB) surface must be clean of fluxes and other residues. In addition, ionic contamination left by flux residues can lead to corrosion and dendrite growth, two common causes of electronic opens and shorts. Other residues can lead to unwanted impedance and physical interference with moving parts.
Technical Library | 2020-06-02 15:16:51.0
A commercial systems manufacturer working on a major defense program contacted the Helpline for urgent assistance with an issue of failed parts during reliability testing. They were attempting to incorporate commercial off-the-shelf (COTS) computer-related hardware into a battlefield system and were experiencing reliability issues. It was noted that the parts were labeled by the vendor as "compliant to military (or MIL) standards" but not clearly identified as tin-lead or lead-free. ACI Technologies has supported a number of customers with lead-free issues and we assisted the customer in developing a short term and long-term solution to their problem.
Technical Library | 2019-06-20 07:45:19.0
One of the two basic risks of employing the commercially accepted, Restriction of Hazardous Substances (RoHS) compliant, lead-free (Pb-free) electronics is the threat to the electronics reliability from the growth of tin whiskers. The other basic risk deals with Pb-free solder joint reliability.
Technical Library | 2019-06-21 10:39:15.0
Recently, an ACI Technologies (ACI) customer called to discuss failures that they had observed with some through-hole capacitor parts. The components were experiencing failures following vibration and accelerated stress testing. Upon receipt of the samples, ACI performed three levels of inspection and Energy Dispersive Spectroscopy (EDS) testing to investigate the root cause of the failures. These analyses enabled ACI to verify the elements comprising the solder joints and make the following recommendations in order to prevent future occurrences. The first inspection was to investigate the capacitor leads using optical microscopy, and no anomalies were found that could indicate bad parts from the vendor or improper handling prior to assembly. However, vertical fill in the barrel of the plated through-holes was too close to the IPC-A-610 minimum specification of 75% to determine a pass/fail condition, and therefore required further investigation.
Technical Library | 2015-07-14 21:32:04.0
The PCB industry is ever changing and adapting to new technologies. OEM specifications and requirements have also advanced due to these technologies. In some cases the OEMs are asking for a low resistance test to be performed on some or all electrical test nets of the PCB or on the holes of the PCB. This requirement is typically not well defined on the fabrication drawing and that leads to misleading conclusions by the fabrication house (...) This paper will use the data gathered by the company’s operations to outline what a 4-wire Kelvin test is and how it can be used. Several examples will be illustrated of what the 4 wire Kelvin test can and cannot do. A clear definition of what limitations are present during the testing operation will be defined. The paper will assist designers in understanding how the low resistance test can assist them and also identify causes that can identify unwanted concerns/issues.
Technical Library | 2012-02-23 21:16:28.0
Installed for the first time 20 years ago, Automated Optical Inspection (AOI) more recently has become an essential part of our SMT environment. Today, most process engineers are turning to machines as an inspection strategy for addressing quality and pro
Technical Library | 2019-10-24 14:23:49.0
Presentation given by Fred Dimock during a seminar at the American Competitiveness Institute, ACI. •Recipe vs. Profile •Material Properties •Why profiles are shaped like they are. •Obtaining profiles •TC Accuracy •Profilers •Test vehicles •Process Window – Eutectic vs. Lead Free •Heat transfer •Oven Control