High density and miniaturized circuit assemblies challenge the solder paste printing process. The use of small components such as 0201, 01005 and μBGA devices require good paste release to prevent solder paste bridging and misalignment. When placing these miniaturized components, taller paste deposits are often required. To improve solder paste deposition, a nano-coating is applied to laser cut stencils to improve transfer efficiency. One concern is the compatibility of the nano-coating with cleaning agents used in understencil wipe and stencil cleaning. The purpose of this research is to test the chemical compatibility of common cleaning agents used in understencil wipe and stencil cleaning processes.Compatibility of Cleaning Agents With Nano-Coated Stencils
Technical Library | 2021-11-17 18:53:50.0
The demand for product miniaturization, especially in the handheld device area, continues to challenge the board assembly industry. The desire to incorporate more functionality while making the product smaller continues to push board design to its limit. It is not uncommon to find boards with castle-like components right next to miniature components. This type of board poses a special challenge to the board assemblers as it requires a wide range of paste volume to satisfy both small and large components. One way to address the printing challenge is to use creative stencil design to meet the solder paste requirement for both large and small components. ... The most important attribute of a stencil is its release characteristic. In other words, how well the paste releases from the aperture. The paste release, in turn, depends on the surface characteristics of the aperture wall and stencil foil. The recent introduction of new technology, nano-coating for both stencil and squeegee blades, has drawn the attention of many researchers. As the name implies, nano-coated stencils and blades are made by a conventional method such as laser-cut or electroformed then coated with nano-functional material to alter the surface characteristics. This study will evaluate nano-coated stencils for passive component printing, including 01005.
Technical Library | 2017-10-26 01:18:49.0
Nano-coatings have been introduced by various manufacturers, with the promise of addressing some of the challenges relative to solder paste printing. Stated benefits include: Reduced underside cleaning, reduced bridging, improved solder paste release and improvements in yield. With several nano technologies already on the market and more likely to be introduced, how can the performance be quantified? How robust are these coatings? How can an assembler approach the ROI of these coatings? What hidden benefits or negative impacts should be considered? This paper will present a rigorous method for evaluating the performance and economic benefits of solder paste stencil nano-coatings.
Technical Library | 2018-03-15 07:23:35.0
The SMT assembly process is continuously challenged by the factors which enhance circuit board performance and limit productivity. The pick and place and reflow systems reflect these driven issues by adding more and more controls to their systems, but the fact is one of the age old processes continues to operate within the same rules since the dawn of the SMT assembly world: The SMT screen printing. (...)This paper showcases a new stencil process that was discovered by reverting to the basics:understanding the reason for each stencil material process, focusing on detailed finishes and a disciplined aperture design process, maintaining original designs, and making the correctly designed apertures to control the paste deposition. The test results drove us to focus the efforts on the aperture walls In this paper we will demonstrate with lab tests SMT process results howthe improved paste release results in improved SMT print process performance and its positive impact on SPI yields and EOL performance.
Technical Library | 2013-06-20 14:33:12.0
With today's consumer technologies driving the need for denser and more compact devices, the assembly process for surface mounted devices has becoming increasingly more difficult. With the mixture of components requiring a broader range of print deposition volume, various techniques are in use in an attempt to ensure consistent and appropriate paste volume is achieved. Some of these techniques include step etching a stencil locally on a targeted device, promoting electroformed smooth wall nickel stencils, through to laser cutting newer grade stencil materials. This paper focuses on the relevant attributes that affect the properties of solder paste release and introduces the effects of surface free energy with respect to key elements that make up the stencil printing process.
Technical Library | 2023-05-22 16:49:42.0
Our customers' issues • Apertures are getting smaller • Paste does not release as well • Contaminates the bottom of the stencil • Increases defects / reduces yield Insufficient solder Bridging Solder balls on surface of PCB Flux residue • Requires more frequent cleaning • Reduced efficiency (wasted time) • Increased use of consumables (cost) USC fabric (use "cheap" fabric to reduce cost) Lint creates more defects Cleaning chemistries (use IPA to reduce cost) IPA breaks down flux and can create more defects
Technical Library | 2018-03-07 22:41:05.0
This study investigates the scooping effect during solder paste printing as a function of aperture width, aperture length and squeegee pressure. The percent of the theoretical volume deposited depends on the PWB topography. A typical bimodal percent volume distribution is attributed to poor release apertures and large apertures, where scooping takes place, yielding percent volumes 100%. This printing experiment is done with a concomitant validation of the printing process using standard 3D Solder Paste Inspection (SPI) equipment.
Technical Library | 2014-03-27 14:50:01.0
Because of the phase out of CFC's and HCFC's, standard solder pastes and fluxes evolved from RA and RMA fluxes, to No-Clean, to low residue No-Clean, to very low residue No-Clean. Many companies came out with their cleaning solutions, aqueous and semi-aqueous, with each product release being more innovative than the previous one. Unfortunately for most of the suppliers of cleaners, two other trends appeared; lead-free soldering and the progressive miniaturization of electronic devices.
Technical Library | 2022-02-16 15:34:32.0
Because of the phase-out of CFCs and HCFCs, standard solder pastes and fluxes evolved from RA and RMA fluxes to No-Clean, to low residue No-Clean, to very low residue No-Clean. Many companies came out with their cleaning solutions, aqueous and semi-aqueous, with each product release being more innovative than the previous one. Unfortunately for most of the suppliers of cleaners, two other trends appeared; lead-free soldering and the progressive miniaturization of electronic devices
Technical Library | 2013-02-07 17:01:46.0
Silicone contamination is known to have a negative impact on assembly processes such as soldering, adhesive bonding, coating, and wire bonding. In particular, silicone is known to cause de-wetting of materials from surfaces and can result in adhesive failures. There are many sources for silicone contamination with common sources being mold releases or lubricants on manufacturing tools, offgassing during cure of silicone paste adhesives, and residue from pressure sensitive tape. This effort addresses silicone contamination by quantifying adhesive effects under known silicone contaminations. The first step in this effort identified an FT-IR spectroscopic detection limit for surface silicone utilizing the area under the 1263 cm-1 (Si-CH3) absorbance peak as a function of concentration (µg/cm2). The next step was to pre-contaminate surfaces with known concentrations of silicone oil and assess the effects on surface wetting and adhesion. This information will be used to establish guidelines for silicone contamination in different manufacturing areas within Harris Corporation... First published in the 2012 IPC APEX EXPO technical conference proceedings.