Technical Library | 2017-11-01 17:06:38.0
Over fifteen years has passed since North America and Europe ceased being the center of worldwide PCB fabrication, and were supplanted by a Far East market with low cost labor, more relaxed environmental requirements, and strong government support. In just a few short years, the superior cost advantages of this new dynamic put volume PCB production in the West out of business, aside for the military and specialty technology applications contained in the few shops that continue to exist today.Recently, however, the conditions which created the current equilibrium appear to be shifting again. In this new dynamic, automation, innovative green wastewater technologies, and next generation process equipment innovations have combined to make new factories capable of achieving rapid ROI for PCB fabrication almost anywhere. This paper means to illustrate this new dynamic, and provide case study examples from the new greenfield installation at the company captive facility in New Hampshire.
Technical Library | 1999-08-09 11:09:42.0
Organic Solderability Preservatives (OSPs), also known as anti-tarnish, on bare copper printed circuit boards (PCBs) are becoming more prevalent in the electronics industry as the low-cost replacement to Hot Air Solder Leveling (HASL). Introducing the anti-tarnish alternative into the customer sites requires working closely with the coating supplier, assembler, and Original Equipment Manufacturer (OEM) to gain a mutual understanding of respective processing concerns and finished product requirements.
Technical Library | 2021-07-06 21:18:02.0
A new PCB surface finish has been developed that offers outstanding performance and excellent environmental protection. This finish has the potential to replace more common finishes such as ENIG, ImAg, ImSn, ENEPIG, or OSP with a chemically resistant plasma deposited coating. The substitution of the wet processes with this dry plasma process offers significant advantages e.g. lower quantities of chemicals used, environmental benefits and improved operator safety.
Technical Library | 2021-07-06 21:13:36.0
The surface finishes commonly used on printed circuit boards (PCBs) have an effect on solder paste performance in the surface mount process. Some surface finishes are non-planar like hot air solder level (HASL) which can lead to inconsistencies in solder paste printing. Other surface finishes are difficult to wet during reflow like organic solderability preservative (OSP). What is the overall effect of surface finish on solder paste performance? Which solder paste is best for each surface finish? It is the goal of this paper to answer these questions.
Technical Library | 2023-04-25 22:03:25.0
This report hopes to achieve several goals: 1. Determine the link between bare PWB contamination, soldered assembly contamination and long-term product reliability. 2. Establish measurable limits for bare PWB cleanliness as well as process control limits for both an aqueous as well as a water-soluble soldering process. 3. Determine whether there is any correlation between common, industry-accepted rose/modified rose (omegameter/ionograph type) testing and long term product reliability. 4. Determine the effect PWB plating finish (HASL, Immersion Silver and Cu OSP) has on both bare PWB contamination as well as soldered assembly in a no clean and water soluble process. 5. Determine whether there is a link between percentage of saponifier used to wash soldered assemblies and long-term reliability. 6. Establish a more cost-effective test for manufacturers to use as a process-monitoring tool.
Technical Library | 2023-07-25 16:42:54.0
Printing solder paste for very small components like .3mm pitch CSP's and 01005 Chip Components is a challenge for the printing process when other larger components like RF shields, SMT Connectors, and large chip or resistor components are also present on the PCB. The smaller components require a stencil thickness typically of 3 mils (75u) to keep the Area Ratio greater than .55 for good paste transfer efficiency. The larger components require either more solder paste height or volume, thus a stencil thickness in the range of 4 to 5 mils (100 to 125u). This paper will explore two stencil solutions to solve this dilemma. The first is a "Two Print Stencil" option where the small component apertures are printed with a thin stencil and the larger components with a thicker stencil with relief pockets for the first print. Successful prints with Keep-Outs as small as 15 mils (400u) will be demonstrated. The second solution is a stencil technology that will provide good paste transfer efficiency for Area Ratio's below .5. In this case a thicker stencil can be utilized to print all components. Paste transfer results for several different stencil types including Laser-Cut Fine Grain stainless steel, Laser-Cut stainless steel with and w/o PTFE Teflon coating, AMTX E-FAB with and w/o PTFE coating for Area Ratios ranging from .4 up to .69.
Technical Library | 2017-02-28 12:39:50.0
During the last 5 years mobile phones and other portable consumer electronics have been extremely popular and spread all over the world in different climate zones in very high volumes. At the same time the mobile phone terminal for many people has become a necessity that is brought with them in any activity they practice. These changes in user behavior have heavily changed the impact on handheld terminals from moisture, sweat, corrosive atmospheres and mechanical drop. As a result of this the requirement to solder joint reliability, corrosion stability and wear resistance are heavily increasing to keep a high reliability of the terminal.Immersion Ni/Au has been the overall dominant surface finish on Printed Wiring Boards (PWB's) for the last 10 years, but a paradigm shift to avoid use of this thin and porous surface finish is ongoing nowadays because it can’t address these challenges in a satisfactory way.In today's handheld terminals, Organic Solder Preservative (OSP) has replaced Immersion Ni/Au on solder pads. Carbon surface finish for Key- and spring contact-pads, combined with the right concept design can make use of Immersion Ni/Au unnecessary in the near future. The result will be higher reliability with less expensive and simpler processes.This paper will discuss the various considerations for choice of surface finish and results from the feasibility studies performed.
Technical Library | 2020-10-27 02:07:31.0
For companies that choose to take the Pb-free exemption under the European Union's RoHS Directive and continue to manufacture tin-lead (Sn-Pb) electronic products, there is a growing concern about the lack of Sn-Pb ball grid array (BGA) components. Many companies are compelled to use the Pb-free Sn-Ag-Cu (SAC) BGA components in a Sn-Pb process, for which the assembly process and solder joint reliability have not yet been fully characterized. A careful experimental investigation was undertaken to evaluate the reliability of solder joints of SAC BGA components formed using Sn-Pb solder paste. This evaluation specifically looked at the impact of package size, solder ball volume, printed circuit board (PCB) surface finish, time above liquidus and peak temperature on reliability. Four different BGA package sizes (ranging from 8 to 45 mm2) were selected with ball-to-ball pitch size ranging from 0.5mm to 1.27mm. Two different PCB finishes were used: electroless nickel immersion gold (ENIG) and organic solderability preservative (OSP) on copper. Four different profiles were developed with the maximum peak temperatures of 210oC and 215oC and time above liquidus ranging from 60 to 120 seconds using Sn-Pb paste. One profile was generated for a lead-free control. A total of 60 boards were assembled. Some of the boards were subjected to an as assembled analysis while others were subjected to an accelerated thermal cycling (ATC) test in the temperature range of -40oC to 125oC for a maximum of 3500 cycles in accordance with IPC 9701A standard. Weibull plots were created and failure analysis performed. Analysis of as-assembled solder joints revealed that for a time above liquidus of 120 seconds and below, the degree of mixing between the BGA SAC ball alloy and the Sn-Pb solder paste was less than 100 percent for packages with a ball pitch of 0.8mm or greater. Depending on package size, the peak reflow temperature was observed to have a significant impact on the solder joint microstructural homogeneity. The influence of reflow process parameters on solder joint reliability was clearly manifested in the Weibull plots. This paper provides a discussion of the impact of various profiles' characteristics on the extent of mixing between SAC and Sn-Pb solder alloys and the associated thermal cyclic fatigue performance.
| 1 |