Technical Library | 2019-12-26 19:13:52.0
Plated through hole (PTH) plays a critical role in printed circuit board (PCB) reliability. Thermal fatigue deformation of the PTH material is regarded as the primary factor affecting the lifetime of electrical devices. Numerous research efforts have focused on the failure mechanism model of PTH. However, most of the existing models were based on the one-dimensional structure hypothesis without taking the multilayered structure and external pad into consideration.In this paper, the constitutive relation of multilayered PTH is developed to establish the stress equation, and finite element analysis (FEA) is performed to locate the maximum stress and simulate the influence of the material properties. Finally, thermal cycle tests are conducted to verify the accuracy of the life prediction results. This model could be used in fatigue failure portable diagnosis and for life prediction of multilayered PCB.
Technical Library | 2021-06-02 19:39:14.0
With an estimated value creation potential for manufacturers and suppliers of USD 3.7 trillion in 2025,1 high hopes are set on Industry 4.0 to bring the next industrial revolution to discrete manufacturing. Yet, only about 30 percent of companies are capturing value from Industry 4.0 solutions at scale today. Approaches are dominated by envisioning technology development going forward rather than identifying areas of largest impact and tracking it back to Industry 4.0 value drivers. Further governance and organizational anchoring are often unclear. Resulting hurdles related to a lack of clarity regarding business value, limited resources, and an overwhelming number of potential use cases leave the majority of companies stuck in "pilot purgatory."
Technical Library | 2021-08-25 16:28:36.0
In this study, a Sn–Bi composite solder paste with thermosetting epoxy (TSEP Sn–Bi) was prepared by mixing Sn–Bi solder powder, flux, and epoxy system. The melting characteristics of the Sn–Bi solder alloy and the curing reaction of the epoxy system were measured by differential scanning calorimeter (DSC). A reflow profile was optimized based on the Sn–Bi reflow profile, and the Organic Solderability Preservative (OSP) Cu pad mounted 0603 chip resistor was chosen to reflow soldering and to prepare samples of the corresponding joint. The high temperature and humidity reliability of the solder joints at 85 #14;C/85% RH (Relative Humidity) for 1000 h and the thermal cycle reliability of the solder joints from
Technical Library | 2021-09-07 08:21:37.0
Utsource grows from a child to an adult serving the global 30W + customers. UTSOURCE.net is a professional purchasing B2B & B2C tools in electronic components field. UTSOURCE.net provides different types such as IC, Modules, RF transistors etc., and various product type's PDF parameter form as well as the related photographs, we also provide satisfying one-stop package service for customers. We fell honored to serve the global 30W + customers.We spent 15 years touching the needs of customers from all over the world.So we know better that our customers need their packages to arrive safely.After-sales service need at your fingertips and intimate service should be to customers' satisfaction
Technical Library | 2022-12-23 20:44:54.0
One of the upcoming reliability issues which is related to the lead-free solder introduction, are the headin-pillow solderability problems, mainly for BGA packages. These problems are due to excessive package warpage at reflow temperature. Both convex and concave warpage at reflow temperature can lead to the head-in-pillow problem where the solder paste and solder ball are in mechanical contact but not forming one uniform joint. With the thermo-Moiré profile measurements, this paper explains for two flex BGA packages the head-in-pillow. Both local and global height differences higher than 100 µm have been measured at solder reflow temperature. This can be sufficient to have no contact between the molten solder ball and solder paste. Finally, the impact of package drying is measured
Technical Library | 2024-04-22 20:16:01.0
The solid-state electronics industry faces relentless pressure to improve performance, increase functionality, decrease costs, and reduce design and development time. As a result, device feature sizes are now in the nanometer scale range and design life cycles have decreased to fewer than five years. Until recently, semiconductor device lifetimes could be measured in decades, which was essentially infinite with respect to their required service lives. It was, therefore, not critical to quantify the device lifetimes exactly, or even to understand them completely. For avionics, medical, military, and even telecommunications applications, it was reasonable to assume that all devices would have constant and relatively low failure rates throughout the life of the system; this assumption was built into the design, as well as reliability and safety analysis processes.
Technical Library | 2024-06-23 22:03:59.0
The melting temperatures of most lead-free solder alloys are somewhat higher than that of eutectic Sn/Pb solder, and many of the alloys tend to wet typical contact pads less readily. This tends to narrow down the fluxing and mass reflow process windows for assembly onto typical organic substrates and may enhance requirements on placement accuracy. Flip chip assembly here poses some unique challenges. The small dimensions provide for particular sensitivities to wetting and solder joint collapse, and underfilling does not reduce the demands on the intermetallic bond strength. Rather, the need to underfill lead to additional concerns in terms of underfill process control and reliability. Relatively little can here be learned from work on regular SMT components, BGAs or CSPs.
Technical Library | 2014-07-02 16:46:09.0
Growth behaviors of intermetallic compounds (IMCs) and Kirkendall voids in Cu/Sn/Cu microbump were systematically investigated by an in-situ scanning electron microscope observation. Cu–Sn IMC total thickness increased linearly with the square root of the annealing time for 600 h at 150°C, which could be separated as first and second IMC growth steps. Our results showed that the growth behavior of the first void matched the growth behavior of second Cu6Sn5, and that the growth behavior of the second void matched that of the second Cu3Sn. It could be confirmed that double-layer Kirkendall voids growth kinetics were closely related to the Cu–Sn IMC growth mechanism in the Cu/Sn/Cu microbump, which could seriously deteriorate the mechanical and electrical reliabilities of the fine-pitch microbump systems
Technical Library | 2015-07-16 17:24:23.0
Qualification of electronic hardware from a corrosion resistance standpoint has traditionally relied on stressing the hardware in a variety of environments. Before the development of tests based on mixed flowing gas (MFG), hardware was typically exposed to temperature-humidity cycling. In the pre-1980s era, component feature sizes were relatively large. Corrosion, while it did occur, did not in general degrade reliability. There were rare instances of the data center environments releasing corrosive gases and corroding hardware. One that got a lot of publicity was the corrosion by sulfur-bearing gases given off by data center carpeting. More often, corrosion was due to corrosive flux residues left on as-manufactured printed circuit boards (PCBs) that led to ion migration induced electrical shorting. Ion migration induced failures also occurred inside the PCBs due to poor laminate quality and moisture trapped in the laminate layers.
Technical Library | 2021-07-27 14:54:26.0
Fast forward to current time. Today, our society embraces cleanliness. We expect, demand, and evaluate cleanliness in almost every aspect of our lives. We wash our cars and pets. We maintain high cleanliness standards in our hotels and public spaces. We require cleanliness in our restaurants and hospitals. We sanitize our hands throughout the day to prevent illness. We live in a clean-centric culture. While we drive clean cars, stay in clean hotels and eat clean food, there is one part of our life where we actually abandoned cleanliness. Many of the circuit assemblies that affect almost every aspect of our daily lives are no longer required to be clean. Even though our life experience confirms the link between cleanliness and reliability, happiness, health, and safety, circuit assemblies no longer maintain that "cleanliness is next to Godliness" status. This was not always the case. There was a time when virtually all circuit assemblies were cleaned. The removal of flux and other process-related contamination was commonplace. Cleaning was as normal as soldering. As we bring history into current time, one may relate the fall of Rome and its adoption of personal hygiene and the subsequent decline in human health to the large-scale abandonment of cleanliness expectations of circuit assemblies and the subsequent reliability issues it has created. How did this happen? Has history repeated itself?