Technical Library | 2023-01-17 17:22:28.0
The impact of voiding on the solder joint integrity of ball grid arrays (BGAs)/chip scale packages (CSPs) can be a topic of lengthy and energetic discussion. Detailed industry investigations have shown that voids have little effect on solder joint integrity unless they fall into specific location/geometry configurations. These investigations have focused on thermal cycle testing at 0°C-100°C, which is typically used to evaluate commercial electronic products. This paper documents an investigation to determine the impact of voids in BGA and CSP components using thermal cycle testing (-55°C to +125°C) in accordance with the IPC- 9701 specification for tin/lead solder alloys. This temperature range is more typical of military and other high performance product use environments. A proposed BGA void requirement revision for the IPC-JSTD-001 specification will be extracted from the results analysis.
Technical Library | 2020-12-07 15:26:06.0
Temperature cycling testing is a method of accelerated life testing done to PCCs that are exposed to normal operation temperature variations over its lifetime. During the testing, intermittent "open" failures can first occur at the hot and cold extremes of the test, exposing weaknesses in the design and assembly. A poor/weak solder joint fatigues, a via trace or barrel cracks, loose connections or a component fails all causing an intermittent open. When not at extreme temperatures, the PCC assembly relaxes, the "open" closes creating electrical connectivity. If you are monitoring the PCC under test in-situ you will know that an intermittent failure has occurred, and the test could be stopped for inspection. If in-situ monitoring was not implemented, you would not know if there were intermittent failures or not. The PCC gets powered up and works fine at room temperature.
Technical Library | 2023-09-16 06:27:24.0
Vacuum reflow ovens are the best way to solder SMD components. They create a controlled environment that prevents oxidation and improves solder joint quality.
Technical Library | 2019-09-03 17:06:09.0
Both optical and scanning electron microscopy (SEM) are powerful tools for failure analysis in electronics and are used for low and high magnification examination. This article will provide detailed, step by step information for examining solder joints.
Technical Library | 2019-06-20 07:45:19.0
One of the two basic risks of employing the commercially accepted, Restriction of Hazardous Substances (RoHS) compliant, lead-free (Pb-free) electronics is the threat to the electronics reliability from the growth of tin whiskers. The other basic risk deals with Pb-free solder joint reliability.
Technical Library | 2019-06-07 14:49:54.0
ACI Technologies was contacted in regards to poor solder joint reliability. The customer submitted an assembly that was exhibiting intermittent opens at multiple locations on a ball grid array (BGA) component. The assembly’s functionality did not survive international shipping, essentially shock and vibration failures, immediately making the quality of the solder joints suspect. The customer was asked about the contract manufacturer and the reflow oven profile as well as the solder paste and surface finish used. The ACI engineering staff evaluated the contract manufacturer’s technique and determined that they were competent in the methods they used for placing thermocouples in the proper locations and developing the reflow oven profile. The surface finish was unusual, but not unheard of, in that it was hard gold over hard nickel, rather than electroless nickel immersion gold (ENIG). The customer was able to supply boundary scan testing data which showed a diagonal row of troublesome BGA pins.
Technical Library | 2019-06-03 15:32:40.0
ACI Technologies was pleased to assist a customer by conducting elemental analysis on several assemblies displaying severe corrosion. Several board assemblies had failed in the field and exhibited areas of corrosion in close proximity to onboard components. The most common source of corrosion on electronic assemblies is residual flux. Fluxes are specific chemistries applied during the soldering process which improve the wetting of the solder to both the pad and component when forming the solder joint. They can be highly reactive chemicals that, if left on the assemblies, can lead to corrosion, electrical degradation, and decreased reliability. In the presence of moisture and electrical bias, flux residue can enable dendritic growth as a result of electrochemical migration (ECM).
Technical Library | 2019-06-21 10:39:15.0
Recently, an ACI Technologies (ACI) customer called to discuss failures that they had observed with some through-hole capacitor parts. The components were experiencing failures following vibration and accelerated stress testing. Upon receipt of the samples, ACI performed three levels of inspection and Energy Dispersive Spectroscopy (EDS) testing to investigate the root cause of the failures. These analyses enabled ACI to verify the elements comprising the solder joints and make the following recommendations in order to prevent future occurrences. The first inspection was to investigate the capacitor leads using optical microscopy, and no anomalies were found that could indicate bad parts from the vendor or improper handling prior to assembly. However, vertical fill in the barrel of the plated through-holes was too close to the IPC-A-610 minimum specification of 75% to determine a pass/fail condition, and therefore required further investigation.
Technical Library | 2020-11-09 16:59:53.0
A customer contacted ACI Technologies regarding a high failure rate of their assemblies. They provided assemblies to be X-rayed and inspected for the purpose of identifying any process related issues such as (but not limited to) solder and assembly workmanship and evidence of damage due to moisture related problems during reflow (a.k.a. "popcorning"). Moisture damage usually appears as physical damage to the component. The first indication of moisture damage would be externally observable changes to the package in the form of bulging or fractures to the outer surface of the component, an example of which is shown in Figure 1. Internally observable indicators of moisture damage typically include fractures to the die inside the package and lifted or fractured wire bonds. These conditions would be apparent during transmissive X-ray inspection. Another symptom of moisture related damage would be inconsistent solder joint sizes that result from package deformation during the liquidus phase of the reflow process. None of these indicators of moisture related damage were present on the customer samples.
Technical Library | 2007-08-16 13:34:31.0
While experienced inspectors may be able to determine the aesthetic differences between a lead-free PCB assembly and a tin-lead version, one cannot rely on the "experienced eye". "Less wetting out to the pad edges" (Figure A) and "graininess and lack of shininess of the solder joint" (Figure B) are typical comments about some lead-free solder joints. However, in cases where a Nitrogen atmosphere was present during the reflow of the solder joint (Figure C), there will be little visual differences between the lead free alloys and their tin-lead counterparts.