Technical Library | 2019-12-05 13:30:46.0
Conformal coatings are regularly employed to protect the surface of a soldered printed circuit board assembly from moisture, chemicals in the PCBA's service environment, and foreign objects or debris. Conformal coatings are nonconductive and therefore cannot be placed on any location where electrical contact will be required, such as connector pins, test points, and sockets. Conformal coatings are also not permitted on any mechanical interface location, such as mounting holes or brackets, to assure the proper fit between items in the final assembly. In order to apply conformal coatings to an assembly and comply with the restrictions on keep-out areas, masking is employed to protect those surfaces.
Technical Library | 2007-02-01 10:08:40.0
The increased replacement of high lead count SMT devices with BGAs and other high ball count area array packages has brought increased challenges to PCB rework and repair. Often solder mask areas surrounding BGA pad areas are damaged when components are removed.
Technical Library | 2013-08-29 19:52:43.0
Au over Ni on Cu is a widely used printed circuit board (PCB) surface finish, under bump metallization (UBM), and component lead metallization. It is generally accepted that less than 3 wt.% Au in Sn-Pb solder joints inhibits formation of detrimental intermetallic compounds (IMC). However, the critical limit for Au content in Pb-free solder joints is not well established. Three surface-mount package platforms, one with a matte Sn surface finish and the others with Ni/Au finish, were soldered to Ni/Au-finished PCB using Sn-3.0Ag 0.5Cu (SAC305) solder, in a realistic manufacturing setting. The assembled boards were divided into three groups: one without any thermal treatment, one subjected to isothermal aging at 125°C for 30 days, and the third group aged at 125°C for 56 days...
Technical Library | 2023-02-13 19:23:18.0
Spontaneously forming tin whiskers, which emerge unpredictably from pure tin surfaces, have regained prevalence as a topic within the electronics research community. This has resulted from the ROHS-driven conversion to "lead-free" solderable finish processes. Intrinsic stresses (and/or gradients) in plated films are considered to be a primary driving force behind the growth of tin whiskers. This paper compares the formation of tin whiskers on nanocrystalline and conventional polycrystalline copper deposits. Nanocrystalline copper under-metal deposits were investigated, in terms of their ability to mitigate whisker formation, because of their fine grain size and reduced film stress. Pure tin films were deposited using matte and bright electroplating, electroless plating, and electron beam evaporation. The samples were then subjected to thermal cycling conditions in order to expedite whisker growth. The resultant surface morphologies and whisker formations were evaluated.
Technical Library | 2015-07-09 17:44:11.0
50,000) number of short duration (
Technical Library | 2019-05-29 01:47:22.0
1.Vias near SMD pads: Solder can flow into the via after melted. As a result cold joint will appear in the end. Check the picture below. 2.Vias on SMD pads: Solder can flow into the via more easier after melted. Check the picture below. 3.Via opening without soldermask covered. When workers solder TH parts by hand, soldering iron can touch vias sometime, then tiny amounts molten solder will stay on vias. This can lead to electrical short easily. We recommend you make all vias tenting (covered by solder mask) if it is possible.
PCBNPI-Professional PCB Fab/PCB Assembly Service Provider From China
Technical Library | 2023-06-12 19:18:24.0
As any new technology emerges, increasing levels of refinement are required to facilitate the mainstream implementation and continual improvement processes. In the case of lead-free processing, the initial hurdles of alloy and chemistry selection are cleared on the first level, providing a base process. The understanding gained from early work on the base process leads to the next level of refinement in optimizing the primary factors that influence yield. These factors may include thermal profiles, PWB surface finishes, component metallization, solder mask selection or stencil design.
Technical Library | 2008-04-08 17:42:27.0
Concern about the failure of lead-free BGA packages when portable devices such as cell phones are accidentally dropped and a general concern about the resistance of these packages under shock loading has prompted an interest in the impact strength of the soldered BGA connection. This paper reports the results of the measurement of the impact strength of lead-free 0.5±0.01mm diameter BGA spheres on 0.42mm solder mask defined pads on copper/OSP and ENIG substrates using recently developed equipment that can load individual BGA spheres at high strain rates in shear and tension.
Technical Library | 2010-03-18 14:02:03.0
Selecting products that have been qualified by industry standards for use in printed circuit board assembly processes is an accepted best practice. That products which have been qualified, when used in combinations not specifically qualified, may have resultant properties detrimental to assembly function though, is often not adequately understood. Printed circuit boards, solder masks, soldering materials (flux, paste, cored wire, rework flux, paste flux, etc.), adhesives, and inks, when qualified per industry standards, are qualified using very specific test methods which may not adequately mimic the assembly process ultimately used.
Technical Library | 1999-07-21 09:04:04.0
A high volume manufacturer of printed circuit boards (PCBs) had attempted for many years to locate an adhesive that was robust enough to meet their manufacturing needs. This proved to be a challenge because they needed the adhesive to accommodate a wide range of different dispensing equipment and board designs. The two key performance criteria required from the adhesive were dispensability and adhesion...