Technical Library | 2016-11-30 21:30:50.0
Mid-chip solder balling is a defect typically associated with solder paste exhibiting poor hot slump and/or insufficient wetting during the reflow soldering process, resulting in paste flowing under the component or onto the solder resist. Once molten, this solder is compressed and forced to the side of the component, causing mid-chip solder balling.This paper documents the experimental work performed to further understand the impact on mid-chip solder balling from both the manufacturing process and the flux chemistry.
Technical Library | 2007-09-06 11:03:33.0
EFD Inc. and Leister USA have collaborated to bust the myth that you cannot perform laser reflow with solder paste. Using Leister diode lasers, EFD has formulated solder pastes that survive the rapid reflow cycle typical of laser heating. These solder pastes reflow and wet well, without spatter, even when heating is accomplished in less than half a second. The flux core in wire solders cannot boast such flux spatter resistance in such an aggressive heating environment.
Technical Library | 1999-05-07 11:24:21.0
Many manufacturers have now completed the conversion to no clean solder paste. Many factors governed this initial conversion, among those being cosmetics, solder ability, and process ability. In circuit testing or probing through no clean solder paste residues has topically not been a major factor in the conversion decision for several reasons. Due to board design, solder paste was only used on one side of the board and not subjected to testing...
Technical Library | 2014-06-05 16:44:07.0
Stencil printing capability is becoming more important as the range of component sizes assembled on a single board increases. Coupled with increased component density, solder paste sticking to the aperture sidewalls and bottom of the stencil can cause insufficient solder paste deposits and solder bridging. Yield improvement requires increased focus on stencil technology, printer capability, solder paste functionality and understencil cleaning.(...) The purpose of this research is to study the wipe sequence, wipe frequency and wipe solvent(s) and how these factors interact to provide solder paste printing yield improvement.
Technical Library | 2007-01-03 16:36:58.0
Solder paste dispensing is not a new process. However, today's microelectronics present a daunting array of technical challenges to meet deposit size requirements. The need for better paste formulations, more precise equipment, and more tightly controlled processes is driving paste suppliers and equipment suppliers to develop new methods and materials. The most challenging solder paste deposits are those smaller than 0.25mm in diameter and today’s electronics demand such deposits. This paper addresses the process requirements for solder paste micro-deposits in terms of material, equipment and process variable control required for success in producing 0.25mm and smaller deposits.
Technical Library | 2013-03-12 13:25:18.0
High density and miniaturized circuit assemblies challenge the solder paste printing process. The use of small components such as 0201, 01005 and μBGA devices require good paste release to prevent solder paste bridging and misalignment. When placing these miniaturized components, taller paste deposits are often required. To improve solder paste deposition, a nano-coating is applied to laser cut stencils to improve transfer efficiency. One concern is the compatibility of the nano-coating with cleaning agents used in understencil wipe and stencil cleaning. The purpose of this research is to test the chemical compatibility of common cleaning agents used in understencil wipe and stencil cleaning processes.Compatibility of Cleaning Agents With Nano-Coated Stencils
Technical Library | 2018-11-06 12:42:25.0
Solder paste is a homogeneous, stable suspension of solder powder particles suspended in a flux binder, and is one of the most important process materials today in surface mount technology (SMT). By varying the solder particle size, distribution and shape, as well as the other constituent materials, the rheology and printing performance of solder pastes can be controlled. Paste flow behavior is very important in defining the printing performance of any paste.The purpose of this paper is to study the rheological behavior of SAC (Sn-Ag-Cu) solder paste used for surface mount applications in the electronic industry. The reason why the rheological tests are presented in this paper are two critical sub-processes: aperture filling and paste withdraw. In this paper, we report on the investigation of the rheological profiles, the serrated cone-to-plate system was found as effective in parameter minimizing the wall-slip effect
Technical Library | 2010-05-12 16:21:05.0
Numerous studies have shown that greater than 60% of end of line defects in SMT assembly can be traced to solder paste and the printing process. Reflowing adds another 15% or so. In light of this fact, it is surprising that no simplified procedure for solder paste evaluation has been documented. This paper is about such a procedure.
Technical Library | 2017-12-27 22:52:43.0
To compensate for the insufficiency and instability of solder paste dispensing and printing that are used in the SMT production process, a noncontact solder paste jetting system driven by a piezoelectric stack based on the principle of the nozzle-needle-system is introduced in this paper, in which a miniscule gap exists between the nozzle and needle during the jetting process.
Technical Library | 2021-05-13 16:09:02.0
The 2017 iNEMI Board and Assembly Roadmap forecasts that, due to economic, environmental and technical drivers, use of low temperature solder pastes will increase significantly and reach 10% of all solder paste used for board assembly by 2021.