Technical Library | 2013-01-17 15:34:33.0
The use of an electroless nickel, immersion gold (ENIG) surface finish comes with the inherent potential risk of Black Pad failures that can cause fracture embrittlement at the interface between the solder and the metal pad. As yet, there is no conclusive agreed solution to effectively eliminate Black Pad failures. The case studies presented are intended to add to the understanding of the Black Pad failure mechanism and to identify both the plating and the subsequent assembly processes and conditions that can help to prevent the likelihood of Black Pad occurring.
Technical Library | 2013-10-24 15:47:53.0
Reflow soldering in a nitrogen atmosphere is a common process consideration in surface mount technology assembly. This is because the use of nitrogen in reflow equipment may benefit the process as well as the quality of the end product, where it can increase the reliability of the solder joint. (...) The present study investigated thoroughly the effect of different reflow soldering atmosphere, which is air and nitrogen on IMC formation and growth
Technical Library | 2014-06-26 16:43:12.0
Edgebond adhesives have been widely used by the industry for improving the shock performance of area array packages. Most of the studies focus on the impact of material properties, such as coefficient of thermal expansion (CTE) and glass transition temperature (Tg), on reliability at room temperature. However, the operating temperature of a component on the printed circuit board bonded with edgebond adhesive can be close to or exceed Tg of the adhesive, where the material properties may be very different than at room temperature.
Technical Library | 2016-01-07 19:13:23.0
The purpose of this study is to investigate the effect of plasma surface modification to improve adhesion strength between polytetrafluoroethylene (PTFE) and electroless copper plating. PTFE is widely used in many industries because of its unique electrical, thermal, and mechanical characteristics. However, because of its low surface energy, it is difficult to acquire enough adhesion strength between PTFE and other substances without surface modification. Plasma is well known as one of the surface modification techniques that improve adhesion strength.
Technical Library | 2016-02-18 18:55:09.0
As lead-free alloys shift into high reliability electronics, the issue of tin whisker growth remains a primary concern among those in the industry. Current research shows that there is no perfect alloy for all cases of electronic usage. Industry leaders and researchers continue to study and search for a lead free alloy that is able to withstand harsh environments while maintaining high reliability.
Technical Library | 2017-01-23 21:12:01.0
"Water is not a problem of the future, but a key issue of our time for businesses: In the future, urgent water risks will increase in many areas of the world. A growing population, a changing consumer behavior and climate change will have an immediate impact on the availability and quality of water and thus build further pressure on governments, businesses and societies." (Quote from the summary of the 2014 WWF study "The imported risk. Germany's water risk in the age of globalization.")
Technical Library | 2018-02-07 22:50:31.0
The architecture of vehicle electrical systems is changing rapidly. Electric and hybrid vehicles are driving mixed voltage systems, and cost pressures are making conductor materials like aluminum an increasingly viable competitor to copper. This paper presents tradeoff studies at the vehicle level, and how to automatically generate an electrical Failure Mode Effects and Analysis (FMEA) report, as well as how to optimize wire sizes for both copper and aluminum at the platform level.
Technical Library | 2018-03-07 22:41:05.0
This study investigates the scooping effect during solder paste printing as a function of aperture width, aperture length and squeegee pressure. The percent of the theoretical volume deposited depends on the PWB topography. A typical bimodal percent volume distribution is attributed to poor release apertures and large apertures, where scooping takes place, yielding percent volumes 100%. This printing experiment is done with a concomitant validation of the printing process using standard 3D Solder Paste Inspection (SPI) equipment.
Technical Library | 2021-01-13 21:29:27.0
Developing actuators to drive high-frequency jetting dispensers in the dispensing technology for electronic assembly applications has become a concern in recent years. This study proposed a new jetting dispenser without a displacement amplification mechanism directly actuated by a moving magnet actuator (MMA) to jet small fluid droplets. In this article, the main geometric dimensions of ...
Technical Library | 2021-07-27 14:49:16.0
Conductive anodic filament (CAF) formation, a failure mode in printed wiring boards (PWBs) that are exposed to high humidity and voltage gradients, has caused catastrophic field failures. CAF is an electrochemical migration failure mechanism in PWBs. In this article, we discuss CAF, the factors that enhance it, and the necessary conditions for its occurrence. Published studies are discussed, and the results of historical mean time to failure models are summarized. Potential reasons for CAF enhancement solutions are discussed, and possible directions in which to develop anti-CAF materials are proposed.