Technical Library | 2023-01-17 17:27:13.0
Reflow profile has significant impact on solder joint performance because it influences wetting and microstructure of the solder joint. The degree of wetting, the microstructure (in particular the intermetallic layer), and the inherent strength of the solder all factor into the reliability of the solder joint. This paper presents experimental results on the effect of reflow profile on both 63%Sn 37%Pb (SnPb) and 96.5%Sn 3.0%Ag 0.5%Cu (SAC 305) solder joint shear force. Specifically, the effect of the reflow peak temperature and time above solder liquidus temperature are studied. Nine reflow profiles for SAC 305 and nine reflow profiles for SnPb have been developed with three levels of peak temperature (230 o C, 240 o C, and 250 o C for SAC 305; and 195 o C, 205 o C, and 215 o C for SnPb) and three levels of time above solder liquidus temperature (30 sec., 60 sec., and 90 sec.). The shear force data of four different sizes of chip resistors (1206, 0805, 0603, and 0402) are compared across the different profiles. The shear force of the resistors is measured at time 0 (right after assembly). The fracture surfaces have been studied using a scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS)
Technical Library | 2023-08-14 09:06:53.0
In the operation of SMT mounter, the process and integrity of the nozzle of the mounter will have a significant impact on the performance of the machine. As one of the important components of the SMT machine, it is necessary for us to carry out daily maintenance and upkeep of the SMT nozzle. To ensure that the suction nozzle of the SMT machine is intact before operation, how should we do a good job of maintaining the suction nozzle of the SMT machine during normal use? KINGSUN technical team analysis operation has the following main points: 1.Wipe the surface of the SMT nozzle with a dust-free cloth. 2.The small aperture nozzle can be passed through with a thin steel wire and then blown with an air gun. 3.The surface of the nozzle should not be soaked with corrosive solution such as alcohol, as this may cause the surface to fall off. 4.HOLDER should use a cotton swab to wipe the cavity and not damage the filter screen. 5.Regular addition of special grease to HOLDER claws. 6.According to production, it is best to regularly maintain and do other maintenance regularly. (* Suitable for Yamaha SMT machine nozzles , JUKI SMT machine nozzles, Samsung SMT machine nozzles, Panasonic SMT machine nozzles, Fuji SMT machine nozzles, Siemens SMT machine nozzles etc.) Regarding the SMT machine nozzle daily maintenance operation instructions, KINGSUN share with you here , hoping to be helpful to you. More information about Products please Contact US at jenny@ksunsmt.com or visit www.ksunsmt.com , thanks.
Technical Library | 2013-09-05 17:44:14.0
Surface plasmon polaritons (SPPs) are localized surface electromagnetic waves that propagate along the interface between a metal and a dielectric. Owing to their inherent subwavelength confinement, SPPs have a strong potential to become building blocks of a type of photonic circuitry built up on 2D metal surfaces; however, SPPs are difficult to control on curved surfaces conformably and flexibly to produce advanced functional devices. Here we propose the concept of conformal surface plasmons (CSPs), surface plasmon waves that can propagate on ultrathin and flexible films to long distances in a wide broadband range from microwave to mid-infrared frequencies.
Technical Library | 2023-10-23 18:28:42.0
This application note discusses the Maxim Integrated's wafer-level packaging (WLP) and provides the PCB design and surface-mount technology (SMT) guidelines for the WLP
Technical Library | 2011-02-03 17:58:46.0
First introduced in the year 2000, the 0201 package was sold in significant numbers in the electronics industry by 2003. According to some estimates, it currently accounts for approximately 20% of surface mounted component (SMC) demand worldwide1. This pu
Technical Library | 2011-02-24 19:20:14.0
In the selective soldering process, dross can be detrimental. Dross (and I use this term to encompass all surface contamination) is created in conjunction with the presence of Oxygen in two different areas of the process, and by separate means. Each must
Technical Library | 2013-10-31 17:36:41.0
Multilayer printed circuit boards (PCBs) that utilize high performance materials are inherently far more challenging for a fabricator to build, due to significant material property differences over standard epoxy glass FR4. These unique material characteristics often require higher processing temperatures, special surface treatments (to aid in hole and surface plating), they possess different expansion properties, making layer-to-layer registration more difficult to control, and require many other unique considerations.
Technical Library | 2019-04-17 21:29:14.0
Electroless nickel electroless palladium immersion gold (ENEPIG) surface finish for printed circuit board (PCB) has now become a key surface finish that is used for both tin-lead and lead-free solder assemblies. This paper presents the reliability of land grid array (LGA) component packages with 1156 pads assembled with tin-lead solder onto PCBs with an ENEPIG finish and then subjected to thermal cycling and then isothermal aging.
Technical Library | 2013-01-17 15:34:33.0
The use of an electroless nickel, immersion gold (ENIG) surface finish comes with the inherent potential risk of Black Pad failures that can cause fracture embrittlement at the interface between the solder and the metal pad. As yet, there is no conclusive agreed solution to effectively eliminate Black Pad failures. The case studies presented are intended to add to the understanding of the Black Pad failure mechanism and to identify both the plating and the subsequent assembly processes and conditions that can help to prevent the likelihood of Black Pad occurring.
Technical Library | 2021-01-03 19:24:52.0
Reflow soldering is the primary method for interconnecting surface mount technology (SMT) applications. Successful implementation of this process depends on whether a low defect rate can be achieved. In general, defects often can be attributed to causes rooted in all three aspects, including materials, processes, and designs. Troubleshooting of reflow soldering requires identification and elimination of root causes. Where correcting these causes may be beyond the reach of manufacturers, further optimizing the other relevant factors becomes the next best option in order to minimize the defect rate.
The SMTA membership is a network of professionals who build skills, share practical experience and develop solutions in electronic assembly technologies and related business operations.
Training Provider / Events Organizer / Association / Non-Profit
6600 City W Pkwy
Eden Prairie, MN USA
Phone: 952-920-7682