Technical Library | 2023-04-17 21:37:32.0
Ionic contamination is a leading cause in the degradation and corrosion of electronic assemblies, leading to lifetime limitation and field failure (Fig. 1). Ionic residue comes from a variety of sources shown in Fig. 2 opposite: Examples of ionic contaminants: * Anions * Cations * Weak Organic Acid
Technical Library | 2021-03-10 23:57:29.0
Latent short circuit failures have been observed during testing of Printed Circuit Boards (PCB) for power distribution of spacecraft of the European Space Agency. Root cause analysis indicates that foreign fibers may have contaminated the PCB laminate. These fibers can provide a pathway for electromigration if they bridge the clearance between nets of different potential in the presence of humidity attracted by the hygroscopic laminate resin. PCB manufacturers report poor yield caused by contamination embedded in laminate. Inspections show ...
Technical Library | 2019-05-06 23:13:09.0
Temperature and humidity test chamber has brought a lot of help to many industrial enterprises, but while it brings convenience to us, we should also take good care of them, otherwise they may be brought into the end-of-life phase ahead of time. The way of maintenance is also very simple. After daily use, the equipment is cleaned regularly, but the cleaning of the test chamber is also very skillful. If the operation is wrong, it may also lead to equipment failure. Let‘s learn how to extend the service life of the temperature and humidity test box together. 1, Pls clean the working room with water after each use, then dry the interior with dry cotton cloth. 2, Pls regularly remove dust from the evaporator inside the equipment, and periodically wipe the equipment to ensure clean and tidy. 3, When doing the test, the sample should be uniformly placed onto sample shelves,and the vent should not be blocked to prevent the influence of the test 4, It is necessary to pay attention to the cleaning of water tanks in peacetime, after the test or when the equipment is not intended to be used for a long time, all the water in the tank should be discharged, otherwise it will lead to the formation of scale inside the tank. The water used in the temperature and humidity test chamber must be pure or distilled water, or long-term use may result in a humidifier or internal pipe clogging. Above are the usual use notice of temperature and humidity test chamber, if customer adhere to the above several points,it is really able to prolong the service life of the equipment.
Technical Library | 2023-04-17 21:17:59.0
The purpose of this paper is to evaluate and compare the effectiveness and sensitivity of different cleanliness verification tests for post soldered printed circuit board assemblies (PCBAs) to provide an understanding of current industry practice for ionic contamination detection limits. Design/methodology/approach – PCBAs were subjected to different flux residue cleaning dwell times and cleanliness levels were verified with resistivity of solvent extract, critical cleanliness control (C3) test, and ion chromatography analyses to provide results capable of differentiating different sensitivity levels for each test. Findings – This study provides an understanding of current industry practice for ionic contamination detection using verification tests with different detection sensitivity levels. Some of the available cleanliness monitoring systems, particularly at critical areas of circuitry that are prone to product failure and residue entrapment, may have been overlooked. Research limitations/implications – Only Sn/Pb, clean type flux residue was evaluated. Thus, the current study was not an all encompassing project that is representative of other chemistry-based flux residues. Practical implications – The paper provides a reference that can be used to determine the most suitable and effective verification test for the detection of ionic contamination on PCBAs. Originality/value – Flux residue-related problems have long existed in the industry. The findings presented in this paper give a basic understanding to PCBA manufacturers when they are trying to choose the most suitable and effective verification test for the detection of ionic contamination on their products. Hence, the negative impact of flux residue on the respective product's long-term reliability and performance can be minimized and monitored effectively.
Technical Library | 2009-04-30 18:06:24.0
This presentation surveys the most significant via and via-related laminate failure mechanisms from past to present using data from current induced thermal cycling (CITC) testing, failure analysis, and other sources. The relative life and failure modes of thru vias, buried vias, and microvias (stacked vs. non-stacked) are compared, along with the affect of structure, materials, and peak temperatures on the above. The origin of via-induced laminate failures such as "eyebrow cracks" and Pb free related internal delamination is also explored.
Technical Library | 2009-05-21 13:41:05.0
Failure due to board flex cracks persists as the dominant failure mode in multi-layer ceramic capacitors (MLCC). (...) This paper is intended to show the impact of temperature cycling, high-temperature life tests, and multiple bend exposures to the MLCC with this flexible termination.
Technical Library | 2012-12-14 14:28:20.0
This paper examines the potential failure mechanisms that can damage modern lowvoltage CMOS devices and their relationship to electrical testing. Failure mechanisms such as electrostatic discharge (ESD), CMOS latch-up, and transistor gate oxide degradation can occur as a result of electrical over-voltage stress (EOS). In this paper, EOS due to electrical testing is examined and an experiment is conducted using pulsed voltage waveforms corresponding to conditions encountered during in-circuit electrical testing. Experimental results indicate a correlation between amplitude and duration of the pulse waveform and device degradation due to one or more of the failure mechanisms.
Technical Library | 2013-02-07 17:01:46.0
Silicone contamination is known to have a negative impact on assembly processes such as soldering, adhesive bonding, coating, and wire bonding. In particular, silicone is known to cause de-wetting of materials from surfaces and can result in adhesive failures. There are many sources for silicone contamination with common sources being mold releases or lubricants on manufacturing tools, offgassing during cure of silicone paste adhesives, and residue from pressure sensitive tape. This effort addresses silicone contamination by quantifying adhesive effects under known silicone contaminations. The first step in this effort identified an FT-IR spectroscopic detection limit for surface silicone utilizing the area under the 1263 cm-1 (Si-CH3) absorbance peak as a function of concentration (µg/cm2). The next step was to pre-contaminate surfaces with known concentrations of silicone oil and assess the effects on surface wetting and adhesion. This information will be used to establish guidelines for silicone contamination in different manufacturing areas within Harris Corporation... First published in the 2012 IPC APEX EXPO technical conference proceedings.
Technical Library | 2009-04-09 20:43:09.0
Evidence has come to light that increased solder process temperatures, specifically for lead free solder, are dramatically shortening life expectancy of components; failures do not show up during initial test, but much later on in the products life,
Technical Library | 2015-02-19 16:54:34.0
Pad cratering is an important failure mode besides crack of solder joint as it’ll pass the regular test but have impact on the long term reliability of the product. A new pin pull test method with solder ball attached and positioning the test board at an angle of 30º is employed to study the strength of pad cratering. This new method clearly reveals the failure mechanism. And a proper way to interpret the finite element analysis (FEA) result is discussed. Impact of pad dimension, width and angle of copper trace on the strength is included. Some findings not included in previous research could help to guide the design for better performance
.gif)