Electronics Forum | Mon Jul 28 05:35:17 EDT 2008 | surendra268
What could be the main reasons for De-wetting in reflow process. Can anybody answer
Electronics Forum | Thu Aug 24 13:20:24 EDT 2000 | Murad Kurwa
One of our divisions is having this problem: - De-wetting on the smt pads and componenent termination on the bottom side after top side procssed through reflow. Board finish is immersion silver. ? Any recommendation on what we should check & verify
Industry News | 2021-08-13 12:58:35.0
The SMTA Capital Chapter, Carolinas Chapter and Philadelphia Chapter are excited to host their first ever tri-chapter event, Mid-Atlantic Advanced Learning Session - Failure is Never an Option, A Deep Dive into Failure Analysis.
Industry News | 2016-12-29 06:43:55.0
Conformal Coating Photo Album CD-ROM The photo CD-ROM album featuring over 280 colour images on conformal coating, materials, inspection and defects and is available to allow engineers to create their own training material, PowerPoint files, process documents and standards. The photo CD covers many of the defects listed:
Technical Library | 2021-08-11 01:00:37.0
Conformal coatings and potting materials continue to create issues for the electronics industry. This webinar will dig deeper into the failure modes of these materials, specifically issues with Coefficient of Thermal Expansion (CTE), delamination, cracking, de-wetting, pinholes/bubbles and orange peel issues with conformal coatings and what mitigation techniques are available. Similarly, this webinar will look at the failure modes of potting materials, (e.g Glass Transition Temperature (Tg), PCB warpage, the effects of improper curing and potential methods for correcting these situations.
Technical Library | 2013-02-07 17:01:46.0
Silicone contamination is known to have a negative impact on assembly processes such as soldering, adhesive bonding, coating, and wire bonding. In particular, silicone is known to cause de-wetting of materials from surfaces and can result in adhesive failures. There are many sources for silicone contamination with common sources being mold releases or lubricants on manufacturing tools, offgassing during cure of silicone paste adhesives, and residue from pressure sensitive tape. This effort addresses silicone contamination by quantifying adhesive effects under known silicone contaminations. The first step in this effort identified an FT-IR spectroscopic detection limit for surface silicone utilizing the area under the 1263 cm-1 (Si-CH3) absorbance peak as a function of concentration (µg/cm2). The next step was to pre-contaminate surfaces with known concentrations of silicone oil and assess the effects on surface wetting and adhesion. This information will be used to establish guidelines for silicone contamination in different manufacturing areas within Harris Corporation... First published in the 2012 IPC APEX EXPO technical conference proceedings.
![[SEC] 3D In-line AXI Solution X-eye 6300 X-ray Inspection Machine](https://img.youtube.com/vi/w-_v-XDRKro/sddefault.jpg)
3D In-line Automated X-ray Inspection system (machine) Model: X-eye 6300 X-ray Tube: 160kV / 500 µa Table Size: Max. 330 x 250mm Min. 50 x 50mm Detector: 12 inch FPXD Defection type (Application): BGA, PoP, chip, QFN, QFP, etc. - High-speed In-lin
ASYMTEK Products | Nordson Electronics Solutions | https://www.nordson.com/en/divisions/efd/resource-center/solder-glossary-of-terms
. De-soldering The removal of solder and components from a circuit, usually for purposes of repair. De-wetting A condition where molten solder has coated a surface and then receded, leaving irregularly shaped mounds of solder separated by areas covered with a thin solder film