Layer: 8 layers Material: FR-4 Board Thickness: 0.6mm Surface Finish: Immersion Gold 1~4u Copper Thickness: 1/3 oz Impedance, 4/4mils width/spacing Layers: 2--36layers Max manufacturing size: 640mm*1100mm Copper foil thickness: 0.5OZ-13OZ M
New Equipment | Design Services
Layer：4 Material：FR-4 4/4/4/4oz Thickness：2.0 Minimum hole：0.35mm Minimum Tracc/Spacing：12mil/15mil Application：power supply Layers: 2--36layers Max manufacturing size: 640mm*1100mm Copper foil thickness: 0.5OZ-13OZ Min line width/space:
Electronics Forum | Sat Sep 20 07:11:28 EDT 2008 | Sean
Hello All, I used to hear that PCB with immersion silver finishing, its non component location pads, tend to be discolour (Yellowish) after went through heat cycle, such as reflow oven. However, if the component solderbility on the PCB is OK, can w
Electronics Forum | Thu Jun 16 17:02:40 EDT 2011 | boardhouse
The finish looks like Immersion Tin or Silver. if its lead free Hot air - could be issue of to high of a Tin Content. find out what brand of Hasl they are using. SL100 Example. Is this tarnished look only being seen after assembly or have you seen
Industry News | 2012-05-04 09:21:15.0
As printed boards evolve and chip speeds increase, the use of microwave technology in commercial applications, such as cell phone towers and in military products, is expanding.
Industry News | 2022-11-11 07:33:41.0
Lyra Reflow Oven is a soft soldering that realizes the mechanical and electrical connection between the solder ends of surface mount components or the pins and the printed board pads by remelting the solder paste pre-distributed on the printed board pads.
Parts & Supplies | Circuit Board Assembly Products
PULANG TECHNOLOGY CO,.LTDOffers electronic manufacturing services including PCB designing, electronic contract manufacturing including electronic product design, electronic product development, electronic product repair, PCB manufacturing, electronic
Technical Library | 2023-08-04 15:27:30.0
A designed experiment evaluated the influence of several variables on appearance and strength of Pb-free solder joints. Components, with leads finished with nickel-palladium-gold (NiPdAu), were used from Texas Instruments (TI) and two other integrated circuit suppliers. Pb-free solder paste used was tin-silver-copper (SnAgCu) alloy. Variables were printed wiring board (PWB) pad size/stencil aperture (the pad finish was consistent; electrolysis Ni/immersion Au), reflow atmosphere, reflow temperature, Pd thickness in the NiPdAu finish, and thermal aging. Height of solder wetting to component lead sides was measured for both ceramic plate and PWB soldering. A third response was solder joint strength; a "lead pull" test determined the maximum force needed to pull the component lead from the PWB. This paper presents a statistical analysis of the designed experiment. Reflow atmosphere and pad size/stencil aperture have the greatest contribution to the height of lead side wetting. Reflow temperature, palladium thickness, and preconditioning had very little impact on side-wetting height. For lead pull, variance in the data was relatively small and the factors tested had little impact.
Technical Library | 2024-04-08 15:46:36.0
A designed experiment evaluated the influence of several variables on appearance and strength of Pb-free solder joints. Components, with leads finished with nickel-palladium-gold (NiPdAu), were used from Texas Instruments (TI) and two other integrated circuit suppliers. Pb-free solder paste used was tin-silver-copper (SnAgCu) alloy. Variables were printed wiring board (PWB) pad size/stencil aperture (the pad finish was consistent; electrolysis Ni/immersion Au), reflow atmosphere, reflow temperature, Pd thickness in the NiPdAu finish, and thermal aging. Height of solder wetting to component lead sides was measured for both ceramic plate and PWB soldering. A third response was solder joint strength; a "lead pull" test determined the maximum force needed to pull the component lead from the PWB. This paper presents a statistical analysis of the designed experiment. Reflow atmosphere and pad size/stencil aperture have the greatest contribution to the height of lead side wetting. Reflow temperature, palladium thickness, and preconditioning had very little impact on side-wetting height. For lead pull, variance in the data was relatively small and the factors tested had little impact.
Lyra Reflow Oven is a soft soldering that realizes the mechanical and electrical connection between the solder ends of surface mount components or the pins and the printed board pads by remelting the solder paste pre-distributed on the printed board
Imagineering, Inc. | https://www.pcbnet.com/blog/understanding-the-pcb-fabrication-process-from-design-to-delivery/
silver’s high electrical conductivity, immersion silver (IAg) has a low signal loss. It’s also RoHS-compliant, but this finish can oxidize and tarnish
ASYMTEK Products | Nordson Electronics Solutions | https://www.nordson.com/en/divisions/efd/resource-center/solder-glossary-of-terms
. Alloy A substance composed of two or more metal elements. Example: Sn96.5 Ag3.0 Cu0.5 is 96.5% Tin, 3.0% Silver, and 0.5% Copper. Generally, alloys will have different properties than those exhibited by their individual elements (e.g