Electronics Forum | Sun Sep 12 12:45:56 EDT 2010 | tony1
Hi there, does anyone experience in NiPdAu solderability dip & look test? I experiencing solder non wet issue on side I/O & also center ground for QFN package. Appreciate someone can offer me a solution. Thanks
Electronics Forum | Fri Sep 19 15:23:33 EDT 2008 | vladig
All I can say is my regular "Get it analyzed", so you'll know what the streak is. Regards, Vladimir
Industry News | 2020-03-19 13:12:42.0
The SMTA is pleased to announce the Best Papers from SMTA International 2019. As speakers at SMTA International, individuals make contributions to the industry by sharing their research and findings. For these exceptional achievements, a cash award and plaque are given to primary authors of all winning papers.
Industry News | 2014-02-03 14:13:04.0
FCT Assembly is pleased to announce that it now offers a variety of anti-tombstoning solder pastes as an option with each of its solder paste fluxes.
Technical Library | 2024-06-19 13:59:50.0
The solderability of a nickel-palladium-gold (Ni-Pd-Au) finish on a Cu substrate was evaluated for the Pb-free solder, 95.5Sn-3.9Ag-0.6 Cu (wt.%, abbreviated Sn-Ag-Cu) and the eutectic 63Sn-37 Pb (Sn-Pb) alloy. The solder temperature was 245ºC. The flux was a rosin-based mildly activated (RMA) solution. The Ni-Pd-Au finish was tested in the as-fabricated condition as well as after exposure to one of the following accelerated storage (shelf life) regiments:
Technical Library | 2022-03-02 21:26:51.0
The solderability of a nickel-palladium-gold (Ni-Pd-Au) finish on a Cu substrate was evaluated for the Pb-free solder, 95.5Sn-3.9Ag-0.6 Cu (wt.%, abbreviated Sn-Ag-Cu) and the eutectic 63Sn-37 Pb (Sn-Pb) alloy. The solder temperature was 245ºC. The flux was a rosin-based mildly activated (RMA) solution. The Ni-Pd-Au finish was tested in the as-fabricated condition as well as after exposure to one of the following accelerated storage (shelf life) regiments: (1) 33.6, 67.2, or 336 hours in the Battelle Class 2 flowing gas environment or (2) 5, 16, or 24 hours of steam aging (88ºC, 90%RH).