Electronics Forum | Thu Apr 21 17:22:29 EDT 2005 | davef
We prefer epoxy.
Electronics Forum | Thu Apr 21 12:35:15 EDT 2005 | jdumont
Well that doesnt sound very promising. What im going to do is make sure these two boards I just coated (with the RTV already cured) will be used in house only. In the future we will do any conformal coating operations before potting with whatever mat
Electronics Forum | Thu Apr 21 10:44:35 EDT 2005 | jdumont
Morning all. So today I have been tasked with conformally coating a few of our first run PCBs for a new product line. The problem is that they have already had all the larger caps potted with RTV. Are there any problems with spraying the CC over the
Electronics Forum | Thu Apr 28 11:14:27 EDT 2005 | bbarr
If you apply the RTV after coating, what happens to bond strength since you are now bonding to the coating and not the board? Will the caps still survive vibration and shock? I specify applying RTV before coating for this reason. Am I correct? I als
Electronics Forum | Thu Apr 21 11:43:03 EDT 2005 | davef
We understand the problem of trying to coat over RTV. We have seen the same problem with acrylic and urethane coatings not wanting to stick to RTV. Some acrylics seem to be worse than urethane. Since this is a new product, may be you could pot your
Electronics Forum | Fri Apr 22 10:12:14 EDT 2005 | davef
Common RTV does out-gas causing corrosion. NASA allows use of non/low-out-gassing RTV. Try the following companies: * Ablestik Electronic: Materials, 20021 Susana Road, Rancho Dominguez, California 90221 U.S.A., 310-764.4600, F 310-764-2545 * Arlon
Electronics Forum | Thu Feb 25 07:37:42 EST 2010 | pcbrown
We are using Humiseal 1B31 and polyester dots for masking. We are spraying this in a Binks sprayer mixed at almost 1:1 with 521 thinner. Whe are seeing the coating creating thin halos around the poly dots as if the dots are "rejecting" the coating. T
Electronics Forum | Wed Jan 03 21:20:22 EST 2007 | davef
Comments are: * General purpose RTV (RTV-108) releases an acetic acid (vinegar) during cure and corrodes copper, brass and sensitive metals. It is therefore NOT for use in delicate electrical or electronic applications. However, there is an electrica
Electronics Forum | Fri Jan 30 10:29:48 EST 2009 | petep
We have a potential new customer who has special PCB requirements. I do not know a lot of details at this point, but have several questions. One of their assemblies has within it , a MID, Solid foil layer, completely isolating one side of the PCB f