Electronics Forum | Thu Oct 07 14:40:31 EDT 1999 | Carol Zhang
I have a board, 4 spacers needed to be soldered on the board first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will be no p
Electronics Forum | Wed Nov 20 07:50:00 EST 2002 | aerineng
Hi, I'm an SMT refugee working in component manufacture - hey, times are hard! I've been asked by a customer to test some of my parts at high temperature on the wave - up to 360 deg Celsius. I've checked my wave and it's only capable of getting up
Electronics Forum | Thu Oct 07 15:39:59 EDT 1999 | Carol Zhang
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Fri Oct 08 16:48:57 EDT 1999 | Dave F
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Tue Oct 12 08:48:16 EDT 1999 | Carol Zhang
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Fri Oct 08 08:26:03 EDT 1999 | Carol Zhang
| | | I have a board, 4 spacers needed to be soldered on the board | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, ther
Electronics Forum | Thu Oct 07 16:57:02 EDT 1999 | Glenn Robertson
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Tue May 12 10:02:52 EDT 2009 | dwl
I am trying to develop a process for building high environmental temperature PCBs (150-225C) specifically for down hole applications. I'm specifying an evaluation board and was thinking about using polyimide PCBs with Sn05Pb92.5Ag2.5 solder. What so
Electronics Forum | Mon Nov 12 15:21:09 EST 2012 | davef
High-temp ball Sn10Pb90 + eutectic solder paste is common place for MLC reflow. Temperatures necessary to alloy the high-temp ball Sn10Pb90 and eutectic solder would be high enough to compromise interposer, board and many components. What are your:
.gif)