Electronics Forum | Mon Mar 21 09:33:25 EST 2005 | davef
RoHS Substance||RoHS MCV Limits||Typical Testing Approaches Lead||1000 ppm* ||Wet chemical digestion followed by ICP (Inductively coupled plasma) or AAS (atomic absorption) spectroscopy ||||XRF (X-ray fluorescence) spectroscopy Cadmium||100 ppm ||Wet
Electronics Forum | Fri Nov 03 07:28:27 EST 2006 | davef
Via filling methods are: * Tenting * Plugging * Capping * Flooding Tented Via. A via covered with dry film soldermask; the via is not filled. When tenting from both sides there may be issues with trapped air that expands during mass soldering. Plug
Electronics Forum | Mon Jul 12 11:35:27 EDT 2004 | Pierre RICHARD
Here are some answers to my questions after a good research. I also added more definitions that could help understand this esoteric language used in assembly, specially surrounding fluxes and their use. In blue italics are comments and extracts from
Electronics Forum | Thu Jun 24 23:57:42 EDT 2004 | George
Could anyone tell me the difference in PCB material Nelco13 and FR4? PCB dielectric material Nelco13 is quite new for me and I knew nothing about it. For imcoming quality control (IQC), I am asked to identify PCB made of FR4 and Nelco13. How to do th
Electronics Forum | Mon Apr 02 01:24:52 EDT 2007 | Haris
Dear all, I want to know the difference between the CSP and the BGA (I think there is only in the mesh pin difference). Secondly, if their solder balls have same dia, LxBxH are also same with the the manufacturing of the pin coating chemical elemen
Electronics Forum | Fri Nov 02 14:46:18 EDT 2012 | ericrr
So how does this (lead free paste Sn42/Bi58) solder compare with the Sn-Ag-Cu (Tin-Silver-Copper) combination which does not flow as well (in the oven), needs higher oven temperature, (that can be adjusted by reducing the oven chain speed) and cost m
Electronics Forum | Wed Mar 19 08:38:13 EDT 2014 | davef
I can't picture much of what you're saying, not for nothing, I'm just not connecting. During assembly, solder mask can affected by heat and chemicals. Typically this would be during: * Soldering * Cleaning I will tell you this: Not to defend assem
Electronics Forum | Tue Mar 25 13:55:05 EDT 2014 | horchak
Ok lets put it this way. If the PCB house used a high quality mask and properly applied it to a properly cleaned surface and properly cured it, then as Dave stated above there are only two things that can destroy it. Excessive heat and overly aggress
Electronics Forum | Wed Dec 08 04:19:16 EST 1999 | pascal MATHIEU
I am working in electronic automotive industry and today we are facing to a very serious problem : if we want to use a PCBoard with a copper thickness of 90�m + fine pitch circuit (0.65mm, 0.5mm) the supplier(several) of the PCB has some trouble t
Electronics Forum | Sat Nov 03 10:57:27 EDT 2012 | davef
EricR: Regarding "*** By the way, since we have used the Tin-Silver-Copper lead free solder there has been a strange liquid type chemical leek from the oven exhausted pipes." ... I don't know anything about your process, but the first thing I'd inve