Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Fri Jul 06 12:11:34 EDT 2007 | james
We are starting to see issues with using Kester WS R562 with lead free components. The joints look grainy on almost all of the 0402'2 and other small components. Some of the solder does not solder to the terminations. These are hybrid boards which
Electronics Forum | Fri Jul 06 12:39:01 EDT 2007 | blnorman
What's the metallization on the board? We use an immersion tin board and had to increase our profile to successfully solder.
Electronics Forum | Wed Jan 07 12:09:40 EST 2004 | Kris
Hi All, Does any body have any information on hot bar lead free soldering ? Need papers or experimental data ASAP Thanks
Electronics Forum | Tue Aug 31 12:01:26 EDT 2004 | russ
Kris, this practice has gone on for years. I have never heard of any problems associated with this. I have heard "grumblings" about tin lead parts being processed with lead free paste, but have seen or heard of no data to support. Russ
Electronics Forum | Tue Aug 31 11:57:03 EDT 2004 | Kris
Hi Any body have any issues soldering tin lead solder paste with lead free terminations ? Components are leaded devices and chip components have read the theoritical discussions on the forum, need to know if any body has seen any real issues tod