Technical Library | 2019-06-19 11:06:46.0
Tin (Sn) metal displays the characteristic of growing “tin whiskers” from pure tin coatings (most actively on relatively thin, electrodeposited or immersion tin coatings), usually months or years from the initial deposition of the tin. Tin whiskers are electrically conductive, filamentary, single crystals of white (beta phase) tin. These filaments of single crystal tin are usually one to five microns in diameter, and a few microns up to several tens of millimeters long, that grow spontaneously from the tin coatings. Alloying additions of several percent (by weight) of lead (Pb) prevents these electrically conductive tin whiskers from growing. Pb alloyed into the Sn was discovered to prevent the occurrence of tin whiskers in electronic assemblies in the 1950s as the Bell Laboratories solution to the problem of tin whiskers. The alloying of the tin with lead has thus quietly averted incalculable losses from short circuits in electronic equipment for the last 60 years.
Technical Library | 2007-04-05 13:48:50.0
Recently a large global player approached us with a problem. They needed an initial assembly solution for brand new components. Their boards and CSP specimens could not safely be soldered due to wetting problems at the solder joints.
Technical Library | 2009-03-25 19:23:18.0
Have you ever been asked to lead a project to fix a problem, implement a new technology or some other initiative? It can be intimidating. Just because you, yourself are a good problem-solver, doesn't mean you have the capacity or drive to work with a team to achieve a goal. Often the secret to success lies in up-front preparation. Here are ten things you can do to help assure that when the project is done, it will have the effective results your leadership team is looking for.
Technical Library | 2013-01-17 15:37:21.0
A problem exists with electroless nickel / immersion gold (ENIG) surface finish on some pads, on some boards, that causes the solder joint to separate from the nickel surface, causing an open. The solder has wet and dissolved the gold. A weak tin to nickel intermetallic bond initially occurs, but the intermetallic bond cracks and separates when put under stress. Since the electroless nickel / immersion gold finish performs satisfactory in most applications, there had to be some area within the current chemistry process window that was satisfactory. The problem has been described as a 'BGA Black Pad Problem' or by HP as an 'Interfacial Fracture of BGA Packages…'[1]. A 24 variable experiment using three different chemistries was conducted during the ITRI (Interconnect Technology Research Institute) ENIG Project, Round 1, to investigate what process parameters of the chemical matrix were potentially satisfactory to use and which process parameters of the chemical matrix need to be avoided. The ITRI ENIG Project has completed Round 1 of testing and is now in the process of Round 2 TV (Test Vehicle) build.
Technical Library | 2019-11-15 02:20:26.0
Material Aging Test-UV Weathering Test Chamber 1.What is UV aging? UV aging chambers use fluorescent ultraviolet lamp as light source to simulate UV radiation and condensation in natural sunlight, and to carry out accelerated weather resistance test in order to obtain the result of weather resistance of the material. UV aging detection is widely used in non-metallic materials, organic materials (such as coatings, paints, rubber, plastics and their products) under the change of sunlight, humidity, temperature, condensation and other climatic conditions to test the aging degree and situation of related products and materials. 2.Why we should do UV aging test? When the product is placed in the ambient environment, there will be different problems taken place, such as appearance changes, including cracking, speckle, powdering or color change, and even performance degradation,which may be due to the loss of components in the resin resulting in chemical bonds changes inside the molecular structure, this is mainly caused by sunlight, industrial exclusion of waste gas, bacteria and so on. The aging performance of the product directly affects the lifespan of the product, so aging test become significant,non-metallic materials, organic materials (such as paints, paints, rubber, plastics and their products) are subject to changes in sunlight, humidity, temperature, condensation and other climatic conditions to test the degree and condition of aging of related products and materials. The natural aging test is to put the plastic specimen under the sun exposure, and it is directly under the natural climate environment,to test the material performance under various factors such as light, heat energy, atmospheric humidity, oxygen and ozone, industrial pollution and the like, the most harsh climate condition should be selected,or near the actual application area of the material, the test site shall be open and flat, no obstacle to affect the test results,the specimen holder shall be facing the equator and at an angle of 45 ° from the ground. When the main performance index of the specimen has been reduced, the test s/b terminated when it achieve the minimum allowable use value . in most case,the test is terminated when the product primary performance index falls to 50% of the initial value. The natural aging process is a very slow process, and there is a great difference in different geographical conditions, which brings difficulties to evaluate the aging resistance of the product. It is an attempt to make an evaluation of the aging performance of the plastic in a shorter time,that is accelerated aging test. The accelerated aging test can be used to simulate the human light source of the fluorescent lamp, including the carbon arc lamp, the xenon arc lamp and the fluorescent ultraviolet lamp, and the artificial light sources can generate more light than the natural sunlight on the ground. When these artificial light sources are used, it is also common to use the combination of the condenser to simulate the rain drop, the dew and the like to conduct the aging test on the product.
| 1 |