Electronics Forum | Tue Jun 16 14:46:25 EDT 2009 | grantp
Hi, If your using NXT to place these BGA's then you must be doing large runs. BGA's are the most easy part to place, and don't worry about them. Just stencil paste down for them as any other component. But we use 1:1 reduction on our stencil, so we
Electronics Forum | Tue Jun 02 21:13:08 EDT 2009 | kircchoffs
thanks for the inputs. we are planning to run on fuji nxt i think cycle time will not be an issue. i still have another question if we can still use the same reflow profile for paste? or do we need to create another profile?
Electronics Forum | Tue Jun 02 07:31:55 EDT 2009 | scottp
Early on when we started looking at BGAs we tried dipping. We've done it in production for a couple decades with flipchips. Dip fluxing BGAs worked fine in the lab but we ended up starting production with screen printed flux for cycle time reasons.
Electronics Forum | Tue Jun 02 22:19:17 EDT 2009 | mikehe
We have been doing BGA's for years now, and I would suggest updating your profile and place a thermal couple on the BGA, keep in mind the bigger the part the more heat it will need, We stencil print all of BGA's from simple bga's to complex ones, you
Electronics Forum | Sun Mar 28 18:49:36 EDT 2021 | mekmat544
Hello, I would like to ask you if there is some formula how to calculate PTH hole and annual ring for pin in paste technology? Thank you. Mekmat.
Electronics Forum | Thu Jun 10 19:10:05 EDT 2021 | kojotssss
Hi, Get your account. https://software.indium.com/stencil-coach/pin-in-paste-apertures.php
Electronics Forum | Fri Nov 08 14:19:59 EST 2019 | dwl
You can try putting titanium stiffeners on the PCB to prevent it from warping. How thick is your stencil? More paste would give you a wider window however too much and you risk bridging. You could try over printing the pad at the heel and toe to get
Electronics Forum | Thu Nov 07 21:28:31 EST 2019 | sssamw
The connector is so long, and has big metal parts, it will be little deformed during reflow I guess, andthe pins planarity should be critical for 200 pins. Did you measure the non wetting pins profile to see if temperature ok? And maybe you can try u
Electronics Forum | Sat Feb 12 09:08:47 EST 2000 | Sal
Experiencing a problem with a 208 PBGA device. I am achieving good wetting with the exception of one ( damn) pin on the outer corner.I have a really good profile but the worrying thing is that it is so inconsistant. Once this open pin failure is dete
Electronics Forum | Sun Feb 13 01:35:55 EST 2000 | Dean
Without further information my first guess would be lack of flux to "cut through" the ENTEK layer. Question: In X-ray is the suspect ball of equal diameter when compared to adjacent balls? If no then the volume of solder is different which would po