Electronics Forum | Tue Jul 24 08:41:16 EDT 2007 | babe7362000
Does anyone out there run the adhesive side first and then the solder side and wash? I was just wondering if this is a good practice or not. I am afraid that we will lose some of the parts, that are just glued on, in the washer? Basically I am try
Electronics Forum | Tue Jul 24 17:15:13 EDT 2007 | blnorman
Unless you've got an extremely agressive cleaner, the epoxy should hold the parts during the delay time. That's their job basically. We ran reflow first pass, glue parts, then wave solder second pass. There were potential delays between adhesive b
Electronics Forum | Tue Jul 24 10:23:36 EDT 2007 | ck_the_flip
Michelle, Traditionally, the adhesive side is always run first since most designers put passives (resistors, caps) on the adhesive (solder side) of the board. I worked in an environment where we did the adhesive side first, sometimes the boards "sa
Electronics Forum | Wed Jul 27 09:58:05 EDT 2011 | davef
Pressure printing systems Conventional stencil printing techniques have fundamental limitations as regards paste handling: The volume of paste available for printing is limited, so frequent replenishment is necessary Paste is difficult to c
Electronics Forum | Thu Apr 17 16:43:09 EDT 2003 | davef
Background: * Bulwith, Ronald A., �Failure Analysis of Solder Joints�, �Insulation/Circuits� magazine, February 1978 * Banks, Donald R., et al., �The Effects of Solder Joint Voiding on Plastic Ball Grid Array Reliability�, Proceedings of the Technica
Electronics Forum | Fri Dec 17 08:05:00 EST 2004 | davef
Your solder paste is talking to you, follow its message. Listen to the paste. Be at one with the paste. If you insist on ignoring the message of the paste, add more paste, if you just need to complete the last board or so, but you really should ju
Electronics Forum | Thu Oct 25 21:04:18 EDT 2001 | davef
You are correct. So, the unit amount of gold [based on IG plating thickness, size of the pad, etc.] dissolves in the solder very quickly. When the solder is liquid for: * A long time, the gold disperses more. * A short time, the gold concentrates a
Electronics Forum | Wed Dec 23 03:33:14 EST 1998 | Charles Stringer
Can anyone recommend a solder stop that can be applied by our PCB supplier. Our current material form Tamura Kaken is causing problems. The material should be capable of withstanding 1 Surface mount IR reflow cycle and 1 wave solder cycle. We need t
Electronics Forum | Fri Feb 02 12:48:29 EST 2024 | spoiltforchoice
Do it all the time. With an automatic printer you would have your two images at opposite edges of the stencil and to switch between them you would remove the stencil and rotate it so the one you want is at the front. Naturally you need to make sure t
Electronics Forum | Tue Dec 29 17:42:27 EST 1998 | Dave F
| Can anyone recommend a solder stop that can be applied by our PCB supplier. Our current material form Tamura Kaken is causing problems. | | The material should be capable of withstanding 1 Surface mount IR reflow cycle and 1 wave solder cycle. | W