Electronics Forum | Tue Nov 01 09:57:18 EST 2005 | Chris
Hi, I am experiencing cracked solder joints on ceramic resonators after the ultrasonic plastic weld process. PCB assy is placed into plastic housing and then housing halves are ultrasonic welded. Not a soldering problem. I know this component is
Electronics Forum | Thu Aug 22 04:56:34 EDT 2019 | hathawayc
Hi,I am a newone here.I wonder if the copper strip can be tin welded on PCB board?How should it be welded?Are there any requirements?Are there any defects?
Electronics Forum | Wed Feb 03 15:50:00 EST 2010 | boardhouse
jamboy, sounds like their have been some quality and personal changes since C-tec was purchased by DDI. I would look at having this board quoted at TTM in Chippewa falls,WI. I have no affiliation with TTM, other than I know that they are able to
Electronics Forum | Wed Aug 09 19:14:15 EDT 2006 | Board House
Our Manufacturing policy regarding welds is as follows. 1) Inner layers - depends on Core thickness and line width. Our shop will not do any welding on core thickness less then 5 mils. or line width less then 5 mil. Good AOI practices reduce the a
Electronics Forum | Wed Mar 05 09:34:32 EST 2003 | HAROLD LICHT
WE HAVE A NEED TO BOND SOME LOW TEMPERATURE LED'S TO A THIN CIRCUIT BOARD LAMINATED TO A HEAT SINK. HAS ANYONE USED AN ULTRASONIC WELDER TO WELD COPPER GUL WING LEADS TO A COPPER PAD USING ULTRASONICS? IF NOT HAS ANYONE USED RESISTANCE SPOT WELDING
Electronics Forum | Tue Feb 11 09:26:57 EST 2020 | astarotf
Hi everyone I have problems welding QFN components in a 10-zone reflux oven, we cannot make a welding fillet that covers the entire QFN pin. Currently we use paste T4 - 63Sn / 37Pb. I enclose the curve of the oven profile. Any help or support on this
Electronics Forum | Sat Jan 19 09:30:45 EST 2002 | davef
Yes, you can rework your thermocouples, but consider using a method other than arc welding. Arc welding can join thermocouples, but it uses a filler. The filler adds a third material that affects the slope of the thermal profile. We rework our the
Electronics Forum | Mon Mar 09 07:29:21 EST 1998 | Tom Mc Grath
Cold Welding I'm presently doing a project on reflow profiling. I came across this expression. Can someone please give me a definition. Best Regards Tom Mc Grath
Electronics Forum | Wed Dec 04 09:46:15 EST 2002 | stefwitt
In a new design project, I would like to attach electronic components to a board using either sonic or resistance spot welding. Anyone out there, who could provide me with actual parameters, like frequency, current and equipment used?
Electronics Forum | Mon Feb 05 17:39:53 EST 2007 | flipit
Remember, deionized water is very corosive. If the water is too deionized, 10 mega ohm, it will leach the ions from exposed metals. I had a stencil cleaner where the welds completely dissolved. The stainless steel tank was fine but the welds were