Electronics Forum | Wed Aug 25 10:49:42 EDT 1999 | Boca
| | Again, I really appreciate the valuable input you all provided. Got my Air-Vac SRM4 machine Friday afternoon. Stored it safely in my cube over the week-end for safe keeping. Tried to find 220V single phase next to air with no luck yesterday. Elec
Electronics Forum | Fri Aug 20 12:18:11 EDT 1999 | Earl Moon
| I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | Can any one tell me what I have to change in my SMT | process (paste, reflow, etc) If any? | I ran one P.C.Boar
Electronics Forum | Fri Aug 20 12:54:11 EDT 1999 | Carol Zhang
| | I am being asked, by my vendor and Purchasing people about converting from Tin/lead pads on P.C.B's to Electroless Tin Plating. | | Can any one tell me what I have to change in my SMT | | process (paste, reflow, etc) If any? | | I ran one
Electronics Forum | Fri Aug 20 00:11:05 EDT 1999 | Rick Holmes
Anyone out there using OSP with double sided reflow and selective solder pallets? I am having trouble testing through what is left of the Entek Plus on the test pads.
Electronics Forum | Fri Aug 20 05:17:25 EDT 1999 | Earl Moon
| Anyone out there using OSP with double sided reflow and selective solder pallets? I am having trouble testing through what is left of the Entek Plus on the test pads. | Think rotary. Earl Moon
Electronics Forum | Thu Aug 12 05:06:12 EDT 1999 | FMung
Hello, Can any netters suggest what critical parameters should be considered & what are there assoicated impacts for a solder paste printing process ... B.Regards, Felix
Electronics Forum | Thu Aug 12 22:31:10 EDT 1999 | Dave F
| Hello, | | Can any netters suggest what critical parameters should be considered & what are there assoicated impacts for a solder paste printing process ... | | B.Regards, | Felix | Felix: There are some 30 variables that affect SMT solder qua
Electronics Forum | Mon Aug 09 10:10:29 EDT 1999 | Gian.D
hello to everybody, we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; does anybody know how to eliminate flux residues or how not to produce them during rework operations? Th
Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Tue Aug 10 20:22:15 EDT 1999 | Wayne Sanita
Hello, Could be that touchup operators are using too much flux. What are you dispensing flux with. Disposable or refillable flux pens are good to have around. | | | | hello to everybody, | | | | we have a really satisfactory no clean proc