Electronics Forum | Mon Jan 18 02:49:03 EST 2016 | nirmex
1-Machine speed. 2-New Head H24 and DYNA Head. 3-New Feeder type W08f 4-New Part Camera. 5-New Y-Axis Flat cable design. 6-New GUI with Touch Screen. 7-Panel Height detection. 8-Feeder raising detection. 9-NPI tools support. 10-Overall machi
Electronics Forum | Fri Jul 14 14:26:04 EDT 2017 | davef
How to clean Durostone wave solder pallet? Add date：2016-1-13 Hits：657 Print Back Ultrasonic machines are often used to clean the pallets. This machine is suitable to eliminate the wax, the oil and other stains. With high efficiency, excellent clea
Electronics Forum | Thu Apr 05 17:06:11 EDT 2018 | stephendo
We recently got a batch wash machine that can use a chemical cleaner. (not a saponifier). NOW I feel confident cleaning no clean boards. Without a machine that can heat water and use a proper cleaning agent, I would not trust cleaning no clean boards
Electronics Forum | Tue Sep 11 16:18:27 EDT 2018 | stephendo
I may be mistaken but I believe that the solvents have defoaming agents in them. I get less foam when I use the solvent than when I don't. If you dissolve the flux in water and agitate it I believe it will foam. I haven't had any over flow issues w
Electronics Forum | Mon Aug 19 11:36:27 EDT 2019 | bulur
How does no-clean flux residues on a PCB assembly impact the ROSE testing? Does no-clean flux residues on the PCBA dissolve in solution of ROSE tester and increase ionic contaminants level in terms of NaCl per surface area? Is ROSE tester solution (a
Electronics Forum | Tue Feb 11 13:27:46 EST 2020 | rgduval
This is a No-Clean solder paste, therefore, it's intended not to be cleaned. If you need your assemblies to be cleaned post assembly, I would highly recommend a water soluble solder paste. It will provide much better looking boards in the long run.
Electronics Forum | Fri Dec 08 19:08:52 EST 2000 | Mike Konrad
I do not know which specific flux you are using, but here are some general guidelines. If your wave soldering machine uses a foam fluxer, then there are foaming agents in the flux. Under �normal� conditions, the volatiles (including the foaming age
Electronics Forum | Wed Jul 18 08:00:48 EDT 2001 | davef
250C flass transition temperature - M = coloring agent or opacifier added to F resin with 110-150C glass transition temperature - N = natural color of resin - P = coloring agent or opacifier added to resin - T = natural color F resin blended with
Electronics Forum | Fri May 21 12:24:21 EDT 1999 | KA Stillings
I normally handle the soldering issues for this facility but a question was asked of me -- What the H@## is this stuff and what is causing it? Was wondering of I could get some input from any Guru on plating issues. Need info ASAP!!!!!!!!!!!!!!!!!!!
Electronics Forum | Tue Sep 22 12:58:18 EDT 1998 | Chyrs
| How can I solve the small solder ball in the N2 W/S ? | The Oxygen level is 10000~20000ppm & no-clean flux. Yuen, Sorry I an't got an answer, just more questions. 1-2% O2 in your wave solder - are you running membrane generated nitrogen? I don't