Electronics Forum | Wed Feb 16 21:51:29 EST 2000 | Dave F
Kurt: Lots of choices, not many of them good, yano. 1 So LPI has taken over the market pretty nearly 100%, but it won't "tent" reliably, because it is not very viscous when applied and drops into the hole. So then, tenting/plugging with LPI is bad
Electronics Forum | Tue Feb 22 10:44:12 EST 2005 | Dougs
when you talk about stencil design, what would you recommend for aperture size on fine pitch if the customer insists on hasl finish on fine pitch devices? i usually use a 10% reduction on everything we have been using ( 16mil pitch and upwards and 0
Electronics Forum | Thu Sep 02 10:24:35 EDT 2004 | dj_jago
Greetings from the UK: I have been quite fortunate to lead (no pun intended) our company towards lead free sooner rater than later. One of our customers produces a product which is refurbushed every 6 months or so and sent back into the market. A
Electronics Forum | Thu Jan 18 21:52:24 EST 2001 | arul2000
>>>>Dave, The BGA substrate surface finish is NiAu, while the PCBA pad surface is HASL. The solder ball composition is SnPb 63/37 and the solder paste used on the PCBA is also the same but with 2% Silver.>>> Dave, sorry I don't have the picture with
Electronics Forum | Fri May 30 18:57:44 EDT 2003 | russ
We place a large amount of .4mm (what is that in microns?)QFPs every day. I would much prefer a BGA package. Reasons are 1. Pitch is greater which provides a larger process window 2. Alignment is easier because you don't need vision for BGA if you
Electronics Forum | Tue Oct 25 11:48:03 EDT 2016 | dontfeedphils
Hi, we're currently running a design with a fairly simple BGA. The problem we're running into is poor solderability (cold looking joints, high voiding in the BGA). All of this on a know good oven, with a known good thermal profile. I'm guessing it
Electronics Forum | Thu Jun 25 09:53:04 EDT 1998 | Earl Moon
| | Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | | Mike | Mike, | You
Electronics Forum | Thu Nov 07 10:59:11 EST 2002 | pjc
IPC-7525 "Stencil Design Guidelines" is a good reference document to have. Here are notes from a Tessera, (a major mBGA mfg.), study- "Application Note Solder Stencil Requirement for mBGA" The stencil aperture is to be square, equal in size to the l
Electronics Forum | Sat Sep 18 12:10:19 EDT 2004 | Steve Gregory
I have a question about solder masking via's in a BGA pattern, and want to see if I'm thinking correctly about this. This problem is kind of along the same line as Carol's problem earlier. I think it's a bad idea to leave the via's free from solder
Electronics Forum | Fri Jun 18 13:55:44 EDT 1999 | Earl Moon
| | Now don't everyone jump on this at once, but it seems time for me to send out copies of my not even close to being dated copy of an article about HASL. Though it was published in 1992, in Printed Circuit Fabrication Magazine, and it got rave revi