Electronics Forum | Wed Apr 26 07:37:34 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from
Electronics Forum | Wed Apr 26 07:37:52 EDT 2006 | amol_kane
"Can we reuse the same machine? My point here is that the non lead free process has already coated the machine interior ( exhaust, internal flow ) with leaded component, and by conversion to lead free are we containminating the lead free product from
Electronics Forum | Sun Dec 26 21:18:04 EST 2004 | tellinghuisen
Chris, We also do not allow the use of Lead-Free BGAs in a lead based process. It is actually one of the things that scares us most about converting to Pb-free. Most of the suppliers that we have talked with are planning on moving to the SAC
Electronics Forum | Wed Apr 26 09:48:32 EDT 2006 | patrickbruneel
Checkout this link http://www.rohsusa.com/ any comments on this??
Electronics Forum | Wed Feb 21 14:14:11 EST 2007 | rgduval
Hi, Bill, Lead-free solder and paste manufacturers will be a great resource for you during the transition; they've tested their products extensively, and their application groups have been able to help me through the biggest changes. There are a fe
Electronics Forum | Fri Oct 31 16:53:30 EST 2003 | Raider
Another well-organized site with loads of info: http://www.smtinfo.net
Electronics Forum | Sun Jul 28 05:35:25 EDT 2013 | mbb
Is it possible to run Pb-Free reflow without nitrogen?
Electronics Forum | Thu Sep 23 16:23:08 EDT 2004 | russ
Pb free pastes do not wet out like 63/37. Their are no claims from any manufacturers that I am aware of that say it will. Your "little solder balls" are likely caused from oxidization during reflow. What type paste are you using 3,4,5? What are t
Electronics Forum | Thu Jan 13 09:55:42 EST 2005 | WDLau
Hi Dave, Then you think it is ok to use leaded (Sn/Pb) BGA with Lead free solder paste (SAC)and reflow process, As someone told it is not reliable and it should not be allowed to go,
Electronics Forum | Thu Sep 30 02:21:29 EDT 2004 | habba
Yes, sorry I forget to mention it. SO only some capacitor will be lead-free. The rest remain 'Pb' parts. The solder paste also remain 'Pb'. You mean that if only this capacitor will change, we can solder that with no problem ? thanks ! habba