Electronics Forum | Thu Nov 21 05:44:07 EST 2002 | kcorrin
We produce several boards with reflowed components on top and bottom. We are finding the solder has wetted to the leads but did not flow completely to the end of the lands. Several factors/causes?: 1) Board warping but paste deposits look good. 2) Mo
Electronics Forum | Thu Feb 28 16:40:04 EST 2002 | liviuj
>Dear SMTneter, >>I am loonkig for some information about how to rework a >>BGA. >>Some technical info explaing how to put solder past >>manualy, soldering manualy, tips and so on. >>Where can I find something about? >>Thanks in advance >>Marcos Hi
Electronics Forum | Wed Apr 28 06:26:15 EDT 2021 | jeremy_leaf
@Evtimov I can't use flux as the components being soldered can't cope with any contamination whatsoever. Even an ultra low solids no-clean flux will be too much. I also can't clean the boards after soldering due to any residual contamination from the
Electronics Forum | Fri Apr 14 13:30:20 EDT 2000 | Murad Kurwa
Hi All: Can you tell me specifically if you converted an exiting product made with Clean process using WS609 or compatible to 'No-Clean' process. We have to convert assemblies from current clean process at a CEM to No-Clean process in our own factor
Electronics Forum | Wed Sep 17 13:00:25 EDT 2008 | mw_fl
For the most part there would not be a lot of change over. There are two primary boards at this time that would be run on the line that also use common components. At this point all but a couple of the pick and place machines we have looked at have t
Electronics Forum | Sat Oct 06 08:32:09 EDT 2001 | davef
Mr. Wizard is not currently available. You get the wizzer. Maybe your dream date will show later. Get your own lab tests done. Show your potential customer that your boards are clean. That�s the issue. The issue is not how you go about cleaning
Electronics Forum | Wed Mar 21 11:42:54 EDT 2012 | davef
Downhole solder suggestions, in order of preference are: * Kester Sn96.3Ag3.7. Most vendors do not stock straight tin-silver alloys, whose wallet is that fat? * SAC305 can usually be used in place of one of the copper-free tin-silver alloys in downho
Electronics Forum | Fri Oct 14 17:54:15 EDT 2005 | Mika
Thanks Patrick for the replay, No, we do not mix the alloys nor Pb pcb:s/RoHS pcb:s in the case I described. It is simply as this: With both the different soldering processes we facing this phenomenon; but whith the RoHS SN100 or SAC305 it turns out
Electronics Forum | Wed May 02 02:41:30 EDT 2007 | May
Of course it is needless to say the performance of SACX0307 is worse than SAC305, and also to some other lead free solders,eg SN100C & SCS7.
Electronics Forum | Fri Jun 23 12:30:24 EDT 2000 | Super K (Evil K)
To answer Gary's question: Gary, you will need a production board, thermal profiler, flux vendors product data sheet on the flux you intend to use, maybe your wave vendor service engineer or wave solder vendor contact (unless you know your wave) and