Electronics Forum | Thu Jun 29 12:07:09 EDT 2017 | georgetruitt
HOW THICK IS THE BOARD? IS THERE A LOT OF COPPER IN THE BOARD? DOES YOUR CUSTOMERS PROVIDE HEAT RELIEF IN THE BOARDS BARREL DESIGN THERE NEEDS TO BE PLENTY OF ROOM FOR LEADFREE SOLDER TO FLOW, DID YOU CHECK YOUR PIN(LEAD)TO HOLE (BARREL) RATIO? N
Electronics Forum | Thu Nov 13 12:49:45 EST 2014 | dyoungquist
I have no experience running a "move the board" selective solder so can not compare the 2 methods..... We have been using an RPS Rhythm "move the pot/nozzle" system since 2008. We are using it solder thru hole components onto boards that often have
Electronics Forum | Fri Apr 28 10:50:26 EDT 2017 | emeto
Hello experts, Here is my problem: I have a board that has smt parts on one side and TH parts on the other. We designed special pallet for wave, but the pallet itself is 15mm thick, so we are still seeing some defects. Have any of you tried to find
Electronics Forum | Mon Apr 25 09:22:15 EDT 2005 | Hiram
Thank you all for your comments always helpful. Have a great week! Hiram
Electronics Forum | Fri May 05 11:55:36 EDT 2017 | emeto
Thank you all! I will ask for quotes and we will see how it goes
Electronics Forum | Fri Mar 22 14:07:00 EDT 2019 | proceng1
I believe that NORDSON now recommends AIM NC277. Nordson bought out ACE-protech.
Electronics Forum | Mon Nov 10 08:53:23 EST 2014 | jpal
We have the opportunity to buy a new selective solder machine and are used to using a very old Jade machine with a moving tank and wetted nozzle. I have two process concept questions: Which is better- move the board over the nozzle or move the nozz
Electronics Forum | Thu Feb 07 12:50:21 EST 2019 | gregcr
Hi All, What are you running for selective solder flux? I'd like any opinion on water soluble and/or no-clean fluxes you are using. In our Kiss 104 machine we use HYDRO-X20 water soluble flux, per the original install suggestion, but I'd like to k
Electronics Forum | Mon May 02 09:21:14 EDT 2005 | jeglum
The beamworks new software on teh 100 is great but went to outstanding when the 60 watt leser was installed and the performance went up 60% in speed. The new software requires the temp of the solder for melting and the ammount to be despenced and the
Electronics Forum | Fri Apr 27 17:51:26 EDT 2007 | chrisgriffin
It appears a disgruntled employee has sabatoged my Sapphire solective solder. Along with cut ribbon cables, I think some jumpers were removed from the system board. D.O.M: '98. I was hoping that some nice person could take a picture of the system b