Electronics Forum | Fri Aug 25 11:29:09 EDT 2006 | mika
Thanks all for Your input. The thing is that we want to avoid to go in to the pattern program and change the height in the middle of running a board. For ex. We start a product, feeders are loaded in advance in the feeder preparation area, operator
Electronics Forum | Wed Jan 17 14:13:31 EST 2007 | jax
You might want to try going to the manufacturer about getting a refurb unit with a warranty. All of the manufacturers listed provide refurbished equipment deals that can be packaged with feeders. If you go with a broker or 3rd party rebuild hous
Electronics Forum | Tue Jan 30 12:58:49 EST 2007 | barryg
We are seeing problems with platinum over silver plated part also. Our main problem is solder splatter under these devices, and voiding at the terminations on parts off the reels.I am curious if you have removed any of these parts and noticed any spl
Electronics Forum | Tue May 08 10:39:42 EDT 2007 | realchunks
Well, in manufacturings defense, I have to say we LIKE our AOI. We run preset-up jobs that are scanned in by the operators. The bar code on each reel is placed there from incoming. Incoming is a very, very busy place. From time to time we find th
Electronics Forum | Fri Nov 09 07:28:48 EST 2007 | jola
We have tested the Feeder Master and I have to say, we are not impressed at all. The main thing that we thought would be great with it was to test the feeders in full speed, but you dont get any data out from the machine so you only end up waching th
Electronics Forum | Tue Jun 17 12:57:26 EDT 2008 | sleech
You are correct. For the 70 deg. C drying temperature to be effective, the relative humidity must be as near to zero as possible. A pulling a vacuum on the chamber is an inexprensive and reliable way to accomplish this. Contrary to some claims, our e
Electronics Forum | Tue Jul 22 20:47:21 EDT 2008 | davef
Q1. Can I do this myself on site? A1. Sure. Most companies demoisturate their components in-house. Q2. Can we use our Vitronics Soltec XPM820 Reflow Oven? A2. You can. Most of us would be using an oven like that in our product processing. If you look
Electronics Forum | Fri Sep 12 04:21:54 EDT 2008 | gsala
Had same problem with SOT23 (two different PNs and Suplliers) problem was random (AVG 0,15%). Parts are RoHS but soldered by SnPb, Lead frame Plating (e3)according to IPC-J-STD609 it means Sn pure (check the label on reel), additional info, it is S
Electronics Forum | Fri Aug 15 22:05:04 EDT 2008 | proy
I am looking for a nice way to print labels, say 1/2"x1 1.5" which I can place on a feeder or IC tube and remove easily later. I am going to set up a laptop on a cart with a small printer and write scripts for my MRP database application so the opera
Electronics Forum | Wed Aug 27 14:19:40 EDT 2008 | grics
Have you given this information to your paste manufacturer???(Profile, Pics of defects?) The profile seems to look ok(without knowing paste info...) I think the ramprate looks a little aggressive but it could be the scaling of the profile and the i