Electronics Forum | Wed Jan 15 21:55:41 EST 2014 | padawanlinuxero
we do that and there's a variation on the solder temp. sometimes around 10 degrees, we have 2 solder pallets that are run in intervals of roughly 3 1/2 minutes a part (the time that take the operator to put all 3 terminals in a 42 pcbs per board, and
Electronics Forum | Wed Feb 20 16:55:52 EST 2008 | flipit
Pd/Ag doesn't usually dissolve (leach) nearly as bad as Ag only. In my hybrid days, we would use 62/36/2 solder. The 2% silver helps saturate the solder joint and thus keep the Ag from being leached away by the Sn.
Electronics Forum | Sat Jun 09 14:28:58 EDT 2001 | Kelvin
No-clean solder paste is definately a trend for tomorrow. However, there are several points you need to consider before you shift from WS to no-clean: 1. Component quality - No-clean solder paste generally (not essentially) get a lower avtivity than
Electronics Forum | Thu Aug 20 18:11:53 EDT 2009 | smt_guy
Hi davef, thanks again for that enlightenment. I'm just curious about what's happening with the solder joint of the said process. Again to add to my unending queries for now: So on top of that copper is a thin layer of lead-free solder composition
Electronics Forum | Tue Dec 08 17:55:51 EST 1998 | Dave F
1. What is the best way to remove polyurethane conformal coating from selected areas? Your conformal coat material supplier is best equipped to tell you how to remove the coating. Polyurethane conformal coating is not easy to remove. Without in-pu
Electronics Forum | Fri Apr 16 11:07:53 EDT 1999 | Vic Lau
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Mar 23 07:35:42 EDT 2010 | jooh
Since I'm new to the forum I probably ask previously answered questions (that I have not found) but I would be grateful if someone could clarify this for me. I'm in R&D at a company where we design low volume (1k-10k) fairly complex PCBAs for our pr
Electronics Forum | Wed Apr 21 22:15:12 EDT 1999 | Chris
| I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is abo
Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Aug 22 21:00:39 EDT 2006 | davef
National says: [ http://www.national.com/packaging/llp/faq.html#faq_manu ] Manufacturing FAQ's Are there any precautions that need to be taken with the LLP package? It is critical to follow National�s guidelines for successful surface moun