Electronics Forum | Tue Nov 19 02:59:24 EST 2002 | yngwie
Hi Experts out there, pls help me with the following matters. How important is the bare PCB baking ? What is the temperature for baking @ what RH ? What would be the impact for the ENTEK finished board should the baking is really necessary ? For t
Electronics Forum | Wed Oct 02 20:59:23 EDT 2002 | davef
We�ve been stewing on this and it just dawned on us the part that�s missing. Blow-holing is caused by BOTH of the following: * Moisture absorption by the resin that holds the board together. [Steve is addressing this with his various baking schemes
Electronics Forum | Tue Aug 26 07:44:06 EDT 2008 | davef
Industry-wide, there is no current requirement for baking of bare boards. It adds no value. * IPC-HDBK-001 has guidelines olden times. * IPC-TM-650 has several test methods to determine moisture resistance to both liquid immersion and absorption from
Electronics Forum | Thu Nov 21 14:17:27 EST 2002 | MA/NY DDave
Hi I can't give you the answer for your question because I have too many questions and would have to know a lot more before I was comfortable giving any advice. I have done mass Baking of piles of PCB's as a needed evil when piles of boards were ex
Electronics Forum | Wed Jul 17 11:45:48 EDT 2002 | fmonette
The current IPC/JEDEC standard J-STD-033 for moisture-sensitive devices does not include a bake cycle at 90C (it includes cycles at 40C and 125C for non-assembled components in reels or trays). However, the upcoming revision, which should be release
Electronics Forum | Fri Nov 22 08:57:56 EST 2002 | davef
Q1: What do you mean by "if the board is manufactured properly"? A2: If the epoxy is noy cured prooperly, for instance, the copper will not be well attached to the glass. So, peel strength will be lower. Q2: I don't believe that the peel off/or lif
Electronics Forum | Wed Nov 20 21:04:15 EST 2002 | yngwie
Hi Dave, What do you mean by "if the board is manufactured properly". If the board is not manufactured properly, humidity will have an impact on the peel strength? Is that what you mean. How does the Humidity impacted the peel strength ? Thru' which
Electronics Forum | Thu Nov 01 00:32:14 EST 2001 | ianchan
we bake boards 80~120 deg-C @1hr, after in-line DI wash. oven setting to 90 deg-C, as +/-5 deg-C, tolerance against door open/shut fluctuations = "temperature loss". If anyone has evidenced procedure, that shows no need for baking, pray do share wi
Electronics Forum | Thu Nov 01 01:48:14 EST 2001 | hamos_wks
168hrs, 1week of storage and frequently applied for rework after testing.
Electronics Forum | Tue Oct 30 21:42:32 EST 2001 | surachai
I have question about board baking after in line washing machine then I would like to know some information that ; 1) Do we need board baking after in line washing machine? Both bare board and assembly borad normally we don't bake . 2)In case of ne