Electronics Forum | Fri Sep 02 05:10:21 EDT 2005 | pyramus
Hi I just would like to ask some assistance how to convert a line using a leaded process to a lead-free process? Is there a need for us to change any equipment? printer/reflow? Currently, we are not yet in full 100% lead-free process yet so most lik
Electronics Forum | Sat Jan 15 10:45:04 EST 2005 | Brad
HI, I actually have ask the same question a while back. Yes, using lead free component in a leaded process should be no problem at all. May required just a little hotter peak temp. during reflow, to achive optimal solderability.
Electronics Forum | Sat Jan 15 23:58:24 EST 2005 | Chua
Could you advise what is the min and max peak temperature for this process. Presently, my leaded peak temperature at the range of 215 - 225 deg.C And how do I know that the solderability is at optimal. Appreciate your help......
Electronics Forum | Thu Jul 19 09:23:52 EDT 2007 | patrickbruneel
Chris, To my knowledge the only difference between leaded and lead-free components is the termination plating. What has changed in the component design that makes them resistant to higher temperatures?
Electronics Forum | Sat Jul 14 08:49:16 EDT 2007 | davef
While you're waiting for others to respond, search the fine SMTnet Archives.
Electronics Forum | Fri Sep 02 05:41:51 EDT 2005 | Rob
Is your oven suitable for Lead free temperatures & can it achieve a decent profile across your complete range of boards? AOI will need to be looked at too as the joints are not as shiney. Cheers, Rob. PS. Where's Thisbie?
Electronics Forum | Mon Jan 17 11:23:49 EST 2005 | Brad
Ya Russ is right for Ti Parts they tend to use more pelladium, which requires a bit more heat average temp increase is about 10 degrees C. from 225-235. As far as optimum solder joint I look for fillets on all sides of leads. The back of the lead is
Electronics Forum | Mon Jul 16 10:26:54 EDT 2007 | davef
Ed: We agree with you that leadfree parts can be used with leaded paste. We disagree that lead part can be used with leadfree paste. Here is link to a previous discussion here on SMTnet on the topic: http://www.smtnet.com/forums/Index.cfm?CFApp=1&M
Electronics Forum | Thu Jul 19 04:38:33 EDT 2007 | chrispy1963
I took a Lead Free troubleshooting Class at SMTA in Chicago last September taught by Phil Zarrow. He told us during that seminar that its not a good practice to cross contaminate Leaded and Lead Free components but IF it is necesary than using lead
Electronics Forum | Thu Jul 19 12:25:51 EDT 2007 | patrickbruneel
Amen to that Hussman. The new lead-free world is not based on science or environment it�s all about $$$$$. And as I said before the promoters of lead-free care less about quality or reliability they just take this great opportunity to double their
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694