Electronics Forum | Fri Oct 19 13:57:17 EDT 2007 | Michael Konrad
Hi Rob, I must take issue with your statement �By definition, no clean solder can be not-cleaned�. All no-clean fluxes can be cleaned. Whether or not one cleans no-clean depends on a variety of factors. More than eighty percent of all post reflow
Electronics Forum | Fri Jan 26 12:57:34 EST 2018 | aqueous
Sorry to disappoint. No-Clean fluxes are resin-based. They are not soluble in water. Water soluble fluxes are by nature Organic Acid and are soluble in water AND must be cleaned within a short period after reflow as they remain conductive and corrosi
Electronics Forum | Sat May 29 16:04:49 EDT 1999 | M Cox
I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-sided
Electronics Forum | Sun May 30 18:52:35 EDT 1999 | Graham Naisbitt
| | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sun May 30 10:15:34 EDT 1999 | Vic Lau
| | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a dou
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Wed Sep 22 02:45:23 EDT 1999 | Brian
| | Dear All, | | | | In order to understand the soldering technologies in SMT, I'd like to understand why some cards are soldered and then cleaned, or only soldered whitout water cleaning nor "ultra sound" wavelength. | | | | I mean that I wonder