Electronics Forum | Thu Jul 14 11:52:16 EDT 2005 | davef
Sure you can use SPC charting on the wave setup parameters to warn of impending problems. Examples of useful points of analysis are: * Dwell * Temperature * Pot analysis Certainly there's a range of other process controls that could be monitored.
Electronics Forum | Wed Aug 23 14:59:32 EDT 2006 | bill
I�ve been lurking on the forum for a while so I will take a stab at this, mainly because there is no answer I take it that you have a variety of boards being produced at the same time and are in fixtures so the conveyors don�t need to be adjusted, a
Electronics Forum | Sat Feb 22 11:37:00 EST 2020 | kylehunter
Hey all, I've made a post in the past about us expanding to a new space, but I wanted to do a new post with specific questions. We currently have a DEK 265, Phillips Opal Xii, and a Heller 1500. Our main reason for expanding is to have a lead-free
Electronics Forum | Mon Jan 15 11:41:56 EST 2007 | davef
Questions are: * Does the component take solder when you dip it in the solder pot to test the solderability of the leads? * Can you get full barrel fill when wave soldering a bare board? * Is your flux reaching the top of the board through the hole b
Electronics Forum | Wed May 21 15:52:24 EDT 2008 | samir
Wow RealChunks! What happened to that firey b#tchey Asian temper of yours? :-) Speak your mind and forever hold your peace! Here's what I know about Lead-Free Wave Soldering: 1.) Hotter pot 2.) Longer dwells Good info. on fluxes, by the way.
Electronics Forum | Thu May 22 16:52:39 EDT 2008 | tonyamenson
Indium got back to me with the attached PDF. I always assumed, that in order to avoid thermal shock, there could not be any more than 80 degrees C difference between the solder pot and the pre-heated board. However, it would seem that any thing le
Electronics Forum | Tue Jan 31 15:51:04 EST 2006 | russ
Relays huh? I can tell you from previous experience that relays are not a good heat gun candidate. Did you check how long this part can withstand the 240? I do not know what the 4 setting is on a liester but it is probably well in excess of the 24
Electronics Forum | Fri Jun 19 10:03:46 EDT 1998 | Earl Moon
| Has anyone had experience with placing BGA on gold plated boards. I thought I read a while ago there was a problem with embrittlment causing cracked joints. If anyone has experience with this your feedback would be great. | Mike Mike, We and ind
Electronics Forum | Fri May 23 18:55:20 EDT 2008 | gregoryyork
This is one of the biggest mistakes with the Lead Free process. We have all listened to the 'industry experts' and followed their advice and unfortunately got it wrong. Keep the dwell times (dependant on alloy selection) the same as Leaded so you are
Electronics Forum | Mon Jun 08 14:19:30 EDT 1998 | Gary Simbulan
Earl, et al, Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. First the caps. We still have
.gif)