Electronics Forum | Fri Dec 09 00:19:51 EST 2016 | aqueous
Hi Dean, We are a manufacturer of cleaning equipment. I'm not sure if your machine is one of ours or another brand. Regardless, I am happy to provide assistance. In order to maximize the level of "helpfulness", it would be helpful for me to know mor
Electronics Forum | Tue Sep 30 13:55:37 EDT 2008 | realchunks
How do you normally solder it?
Electronics Forum | Thu Dec 08 22:57:45 EST 2016 | ttheis
I'm not too experienced with this but what about an air-blast with an ionized air source such as an air knife above and below a conveyor to push most of the fluid off of the pcba then run through an oven just above vaporization temperature.
Electronics Forum | Wed Oct 02 15:20:55 EDT 2002 | Eric
Is there a steadfast rule of thumb for a good solder joint on an Enig Gold board. I come across this number 217C when discussing BGA profiles. Is this a published number? I sure could use a reference. Anybody feedback is appreciated.
Electronics Forum | Wed Oct 02 16:13:05 EDT 2002 | babe
Have you had your solder pot tested? I find that levels of contaminants can rend a solder joint that dull look.
Electronics Forum | Thu Sep 26 14:43:43 EDT 2002 | Jim M.
unsure of what solder spec. your working to?.IPC/EIA J-STD-001C, Section 9.2.4 clearly states dull, matte, gray or grainy appearing solders are accpetable depending on your process and if the acceptability of the neaxt paragraph is met.IPC 610 and J-
Electronics Forum | Wed Oct 02 18:18:58 EDT 2002 | davef
The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This provides for setting your peak based on the
Electronics Forum | Thu Sep 26 11:44:23 EDT 2002 | abelardo
Hello everyone out there in the SMT world. I have a dilema I'm currently running a board that has 3 csp's with a .75 mm. ball pitch and .3mm ball size. And 2 qfp's-160. The stencil is 4 mils thick and I'm using a 63/37 solder paste. My reflow prof
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Fri Mar 19 12:17:15 EDT 2010 | stepheniii
Be carefull if you go to no clean. Or be prepared from complaints from the test department regarding their ICT pins getting dirty.