Electronics Forum | Tue Dec 03 11:59:01 EST 2002 | slthomas
We haven't run a profile yet....probably because we're a-feared to. We can't do topside preheating here to any degree because we use an aluminum plate for aligning hundreds of top side through-hole components (pots, switches, buttons, LEDs) that te
Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Mon Dec 16 16:35:55 EST 2002 | Jim Ferris
Randy, Steve & all, Can you guys point me in the right direction when it come to using selective wave soldering...I am trying to get in-depth information on the Pro's & Con's of having our supplier use this process for our PWA's. (I can see there ar
Electronics Forum | Fri Feb 03 16:40:24 EST 2006 | Mike
At my last employer, we ran a number of tests to make a "Hybrid" profile work (same profile Joe lists) . It worked great for everything but BGAs. The problem (6 months ago) was using parts not rated for lead free reflow temps. As the market fills wit
Electronics Forum | Mon Apr 09 19:50:33 EDT 2012 | action_101
Hello, We're building some boards with 01005's and the only issue we are running into is the solder is not reflowing. It's the damnest thing, we are having no issues with the printing process or placing the components, the two areas we thought we wo
Electronics Forum | Mon Apr 09 20:55:46 EDT 2012 | action_101
I forgot to add that we are using a 3 mil stencil. It seems like to me that may be there isn't enough flux left when we reach liquidous?? About half of the solder spheres do melt and wet on each pad, but the top half of each solder joint is just the
Electronics Forum | Tue Apr 10 04:16:20 EDT 2012 | grahamcooper22
you are seeing a typical issue that is caused when such small volumes of paste are printed....there are several reasons for it..the tiny amount of flux in the small deposit becomes exhausted much quicker then it does in a larger deposit ( the flux ma
Electronics Forum | Mon Dec 17 13:58:54 EST 2007 | ck_the_flip
I made my own wave measuring device using KIC2000 system. KIC2000 has automatic wave detection, so now I have a profiler for both reflow ovens and wave solder. The delmat carrier only cost $500. A guy, Samir, from this forum gave me the idea, actu
Electronics Forum | Mon Jul 28 11:31:42 EDT 2008 | blnorman
Ideal situation is get a technical rep from the solder paste supplier. They know their paste better, and should be able to work out a profile based on their paste and your oven. Again, a technical rep, not the sales guy.
Electronics Forum | Fri Aug 01 21:10:35 EDT 2008 | leo_dektec
You can keep only the 5th zone as the reflow zone. And lower the first two zones to keep a good ramping rate. Meanwhile,please note the ting temperature in software or control panel is not the exact temperature in your PCB, you'd better get a KIC or