Electronics Forum | Wed Nov 14 03:26:38 EST 2012 | spopov
Ryan, in some cases we use 2 pastes with different melting temperature (LF SAC and PbSn)for complex boards with components on two sides. And we want to try to replace LF SAC with low melting paste.
Electronics Forum | Thu Nov 15 09:29:29 EST 2012 | anvil1021
Maybe this piece of information will help. In China (just returned from visit) there are many factories that are using a dual temperature process using SAC305 or Sn100C and 42/58. Apparently this allows them to run their through hole parts through re
Electronics Forum | Thu May 13 16:55:51 EDT 2021 | emeto
With Pb-Free HASL you can't use Pb process for sure as the melting point of tin is so much higher than the lead paste process. SAC305 is the most popular compound, unless your assembly requires something else for a specific reason.
Electronics Forum | Thu May 20 03:45:22 EDT 2021 | jineshjpr
SAC305 Will be the best choice with minimum TAL, Maximum Soak Solder Profile. Surely your solder Joint strength also will be more reliable & This can pass any kind of reliable Tests.
Electronics Forum | Wed Dec 24 15:28:17 EST 2008 | edmentzer
We use SN100C for wave soldering and hand Lead free soldering and have had very good results. The wire cored solder for hand soldering flows good and makes very good solder joints. The SN100C in the wave solder machine also works very good. We use
Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Wed Nov 07 21:36:17 EST 2012 | davef
Multiple process and rework thermal cycles are brutal on boards and components. Improving reliability of products through reducing thermal stress ends-up being a major driver to the interest in lower MP LF solders. Binary LF solders require the addit
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Wed Jan 09 05:21:07 EST 2019 | jrogalski88
I will try this, thank you! Out of curiosity what about an 0807?? currently using an 1140 but there's still issues with that. I'm almost wondering if maybe parts just aren't sitting flat in the pocket so I'm getting pick and visioning issues.
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could