Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Mon Feb 19 15:32:42 EST 2007 | blnorman
We use SnPb paste and bar with leaded and non-leaded component finishes. The predominant finish on components we use is Tin, there are a few NiPdAu. We've had no problems with the component finishes used in the SnPb process.
Electronics Forum | Wed Jul 14 00:50:34 EDT 2004 | Grant Petty
Hi, What's the best process for going lead free? Ordering lead free parts and using them with current paste, and then once all the parts are lead free, moving to lead free paste as well? Then the wave will be fun to change over. What a nightmare th
Electronics Forum | Tue Dec 13 17:41:04 EST 2011 | davef
A Study Of 0201’s And Tombstoning In Lead-Free Systems, Phase II Comparison Of Final Finishes And Solder Paste Formulations http://sheaengineering.com/Documents/APEX%2008%200201s%20and%20Tombstoning%20phase%202%20paper.pdf CONCLUSION The condition
Electronics Forum | Tue Jul 13 06:49:53 EDT 2004 | imtiaz
In one board we are using 213 SMT components out of which 23 components are lead-free and the rest are leaded. The paste used is also leaded. Do we have to make any changes in the profile of our reflow oven ? Also will there be any negative effect on
Electronics Forum | Mon Feb 12 17:05:29 EST 2007 | Jose
Today is more complicate to find components with lead than with "lead free", and the, I think that you have very feww lead components. And, if don�t work on exceptionals companies, you MUST use LEAD FREE PASTE. In one case, or in the opposite, the re
Electronics Forum | Tue Feb 06 21:43:11 EST 2007 | Wayne
If it is instructed to ship lead free product to customer, then low temp lead free solder paste can be considered. For example, Viromet solder paste from Singapore Asahi (peak temp is between 220 to 225 degree C).
Electronics Forum | Thu May 06 10:52:08 EDT 2004 | John S
Many component manufacturers are moving to Pb free terminations. I've been doing a literature study of Pb free processing and have found several articles that indicate Pb-free paste with Sn/Pb terminations leads to early fatigue failures. Does anyo
Electronics Forum | Thu May 13 09:52:34 EDT 2021 | winston_one
Want to update this question a little, I know it appears few years ago, but I hope there is some updates... We have to assembly few samples of motherboards with this kind of finish (customer mistake during pcb order). Normally we can use leaded sold
Electronics Forum | Thu May 01 15:11:37 EDT 2008 | dphilbrick
CK So as I see it batch B represents a leaded process with leaded components and D is a leaded process with lead free components. Batch Components Paste B SnPb Sn62 D Lead-free Sn62 If so it is BETTER to run a lead free BGA with Sn