Electronics Forum | Wed Dec 24 20:29:45 EST 2008 | xianhua_tang
Oh,I consider the process is wrong,it is stencil print paste-mount-reflow -apply glue-reflow,then wave solder. it must pass twice reflow,also the first reflow profile is different and the second .
Electronics Forum | Mon Dec 22 14:15:41 EST 2008 | ck_the_flip
As Emil says, it's 100% the glue! Your paste is not designed to hold parts on at wave solder. Reflow is MUCH hotter than glue, so I doubt you're not adequately heat-curing it. Possibly, the glue cure is "too hot" and maybe making the material brit
Electronics Forum | Fri Nov 02 09:09:56 EDT 2012 | davef
Sure you can use it it with leaded HASL. Recognize that ... * Your Sn42/Bi58 will no linger be Sn42/Bi58 * Your leaded HASL will no longer be the same leaded HASL that walked in the door to your plant * Lead from HASL coatings can diffuse through the
Electronics Forum | Sat Nov 03 11:08:24 EDT 2012 | anvil1021
We have experience with this alloy, but with enig and we did start with PB HASL, none of our PCBs would of course pass thermal cycling at normal temperatures with the HASL so we went to ENIG. we could thermal cycle at 100-115C with no issues. We foun
Electronics Forum | Sat Nov 03 11:20:35 EDT 2012 | davef
EricR: There's substantial information about the properties of solder alloys on the web. Here's an example of something that I clipped from one site Alloy ||Solidus (°C)||Liquidus (C°) ||Tensile Strength (psi / MPa) Sn42 Bi58||-E-||138||8000 / 55.2
Electronics Forum | Sat Nov 03 10:57:27 EDT 2012 | davef
EricR: Regarding "*** By the way, since we have used the Tin-Silver-Copper lead free solder there has been a strange liquid type chemical leek from the oven exhausted pipes." ... I don't know anything about your process, but the first thing I'd inve
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could
Electronics Forum | Fri Oct 01 01:25:55 EDT 2021 | sn
Thank you Djo for your sharing. By the way, do you know that which field/product will prefer to use SAC405 paste instead of SAC305 or lower Ag wt% alloy solder paste?
Electronics Forum | Thu Oct 02 17:00:44 EDT 2008 | davef
Is that accurate? If so, what are your aspect & area ratios? [Similar to the JerryS comment above.] * You say, � � and the average height is very high: nearly 200 pct.� => Our troop can make paste that height too. They snap the stencil-off a fast as
Electronics Forum | Thu May 06 06:47:12 EDT 2004 | praveen
Hi, I just need to undestand any issue? If I mount Pb free BGA and use normal SN/Pb solder paste?