Electronics Forum | Tue Aug 22 03:04:07 EDT 2006 | PP
Any help/suggestion is much appreciated I am doing lots of BGA Reworks from a small uBGA with a few balls to a large BGA with over 1500 balls. The reworks have been done on SRT 1100 Series Machine for many years. SRT 1100 Machine is good for the c
Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Jun 16 15:01:58 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Tue Jun 16 15:00:12 EDT 1998 | Gary Simbulan
There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Wed May 24 15:59:34 EDT 2006 | JohnM
I have a product with mixed in Pb free and Pb BGAs. I decide to use SnPb paste with Pb free reflow profile to make it work for both types of BGA. Do I have a reliability solder joint issue by using this method? How is your opinion on this case? Can
Electronics Forum | Wed Sep 18 18:41:17 EDT 2002 | davef
People have made good comments. Additional points are: * Your bridging is probably being caused by one or more of the following: [1] printing too much paste, [2] smearing the paste during placement or subsequent handling, or [3] paste slump during t
Electronics Forum | Tue Sep 17 15:47:42 EDT 2002 | stepheno
Where I worked previously we had some boards with a couple 15 mil pitch parts. The first batch we got all had undersized pads. We had lots of bridging. We had less bridging with bigger pads. The ball size in the paste makes a bigger diffence regar
Electronics Forum | Thu Sep 19 11:14:45 EDT 2002 | Jim M.
We had lots of problems with bridging on 15.8mm pitch, QFP17-160 at the start.The board was .032 thick, double sided-six boards to a panel. Here is the problems (not neccessarily in the biggest to little but as i remember them) and solutions that he
Electronics Forum | Mon Nov 27 17:47:23 EST 2000 | Dave F
Gyver: Lemme take a wack [if you�ll excuse the expression, given direction of the later discussion] at your questions. Q1. Will the baking of BGA or PCB cause more oxidation before the SMT process? A1. It certainly will not cause less oxidation,