Electronics Forum | Tue Oct 13 16:11:44 EDT 2009 | mikesewell
Not sure how many inspections need to be done at 15 - 20sec total per board, but you may need to install multiple SPIs/AOIs to hit your takt time. Mike
Electronics Forum | Thu Feb 11 20:36:18 EST 2021 | tsauve
1.Yes but you want specific SPI & AOI machines. Same manufacturer can provide both. 2. Yes but not as well as an SPI machine. 3. Don't understand question. 4-7 You should do your research, or hire someone with the expertise you require.
Electronics Forum | Mon Jan 25 01:35:56 EST 2010 | orproadamshaw
Hi, As stated above development of the systems we took over from Orbotech has not ceased. I don't know which geographic region you are in, but your first contact should be either a Business Partner, or ORPRO Vision support direct in the region. On
Electronics Forum | Tue Feb 08 12:36:28 EST 2000 | Charlie
I'm looking for information from both those who do cure glue and reflow past with the same profile and those who have tried and decided against it. What were the problem? What are the limitations?
Electronics Forum | Wed Aug 26 12:02:23 EDT 1998 | Steve Joy
Does anyone have any experience they are willing to share on Ag epoxy used as a copper through hole plating replacement? Was CEM3 used? What are the limitations? Thanks, Steve
Electronics Forum | Wed Oct 28 11:38:00 EDT 2009 | andoe
Does anyone know how to get a printer to work with an MCS30 system. I have limited information about printer setup.
Electronics Forum | Wed Mar 02 18:46:02 EST 2005 | Austinj
The tendancy always has been "when in doubt, touch it up"... this is not the way to "verify the process" and is not the best strategy for multiple reasons (unessecary rework, additional labor costs, as well as making the solder joint more brittle, [i
Electronics Forum | Mon Mar 21 09:33:25 EST 2005 | davef
RoHS Substance||RoHS MCV Limits||Typical Testing Approaches Lead||1000 ppm* ||Wet chemical digestion followed by ICP (Inductively coupled plasma) or AAS (atomic absorption) spectroscopy ||||XRF (X-ray fluorescence) spectroscopy Cadmium||100 ppm ||Wet
Electronics Forum | Tue Nov 25 12:48:31 EST 2014 | cyber_wolf
Has anyone looked at SPI results across different squeegee blade manufacturers ? We are running Momentums and using the MPM pro-blades. Ive been considering looking at permalex blades again to see if I can maybe squeek out some better yields.
Electronics Forum | Thu Jan 18 07:22:10 EST 2024 | klauss
Is there any stardarts to help us what tolerance values (max or min. height, weight, volume etc) should we use while programming AOI and SPI.