Electronics Forum | Fri Jun 22 07:16:37 EDT 2012 | brettrenishaw
Spray fluxing yes but have checked the uniformity by using a fluxometer. Also have put boards through with only flux and preheat. no wave up to see if the carrier is being burnt off. I will look into the skip plating issue. Thanks again
Electronics Forum | Wed Jun 13 06:42:14 EDT 2012 | brettrenishaw
We have a problem with our Unleaded wave solder machine only randomly soldering some pads. I have looked at the flux level and that appears fine aswell as cheking the preheat and solder height in the bath. The probelm is not exclusive to one perticul
Electronics Forum | Thu Jun 14 15:29:29 EDT 2012 | davef
That you can get good solder flow when hand soldering seems to indicate that the temperature of your solder pot is too low. Still, I'm uneasy that you see gold on the pads after passing the board across the solder pot. Gold is so thin with ENIG. So
Electronics Forum | Fri Dec 01 17:03:57 EST 2000 | Dave F
Curious, very curious ... Residues � Where are these residues? [solder & laminate / mask, solder only, laminate / mask only] What is the result of your analysis to the residues? How do you know it�s a flux residue, rather than a chemical by product
Electronics Forum | Wed Oct 11 09:55:10 EDT 2000 | Ian Harrison
Some boards that are populated by one of our subcontractors are getting a white powdery residue forming on them. I think it is the non clean flux and process which they are using that is causing the problem. Their process is as follows. Flux is put i
Electronics Forum | Wed Nov 21 19:45:36 EST 2001 | Yngwie
Hi Guys, I need help. I�ve a trouble with non-wetting problem on the lead of 208 pin, 20 mils pitch QFP. We are on intrusive reflow. I never faced this problem before on this product after running them for about 2 years now. This occurred on one pa
Electronics Forum | Sat Aug 26 12:26:57 EDT 2000 | Ramon I Garcia C
Hi friends: I have a problem in the process of one PCB, I have a lot of insuficients of solder in top of the board, this pcb already was working good, but sudenly began there isn't flow thru hole, I ran the profile and it was ok, if I inmerse i
Electronics Forum | Sat Jun 30 11:28:24 EDT 2001 | davef
Consider using a roll solder with a flux that well matches the residues you can accept to be remaining on the board when you get finished processing. Many people use a no-clean flux cored roll solder for such operations, because they don't want to c
Electronics Forum | Thu Nov 07 14:30:38 EST 2002 | Debi Musante
We have been presented with the task of placing a BGA on top of a PGA. The previous process choice was to apply paste directly on the BGA (which failed functional testing) We are considering applying tacky flux (only) on BGA, since this is our first
Electronics Forum | Sun Jul 26 20:56:43 EDT 1998 | Masdi Muhammad
We are trying to reduce the number of units fail at system test due to flux on gold finger. We know so far that the flux is deposited onto the goldfinger during touch-up or rework and to reduce the contamination we are planning to implement 'tapin