Electronics Forum | Fri Jun 09 08:20:56 EDT 2006 | kehoem@bellsouth.net
We have a board calling out for 50 micro-inches of nickel over 30 micro-inches of gold. This is a solid gold board on Rogers material. ENIG cannot be deposited that thick right? Electroplated gold (we thought) was usually 35-50 micro-inches and was
Electronics Forum | Wed Jul 05 17:06:36 EDT 2000 | Michael Parker
Patrick- You have not given enought detail of the type of discoloration. Is it "white residue"? Can it be "rust" colored? Whatever it is, you fab supplier needs to be called in immediately and give you an exact reason for this failure. Just rubbing
Electronics Forum | Mon Jan 25 21:43:04 EST 1999 | Dave F
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Tue Jan 26 19:43:02 EST 1999 | Ross Berntson
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Tue Jan 26 19:43:26 EST 1999 | Ross Berntson
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Thu Jun 04 11:09:50 EDT 1998 | Justin Medernach
| I have gold fingers that I want to mask when running over the wave without pallets. They're on the leading edge of the board. I recall seeing rubber boots that slid onto the fingers to mask them. Pop 'em on before the wave; pop' em off after and
Electronics Forum | Thu Jun 04 09:53:31 EDT 1998 | Dave F
| I have gold fingers that I want to mask when running over the wave without pallets. They're on the leading edge of the board. I recall seeing rubber boots that slid onto the fingers to mask them. Pop 'em on before the wave; pop' em off after and
Electronics Forum | Thu Jun 06 11:42:24 EDT 2002 | Brad Jakeway
What you are seeing on your gold fingers is referred to as flux spattering. This is a very commond problem with gold fingers if you have a zero flux spattering criteria for quality control. The key to eliminating this problem is in the reflow profi
Electronics Forum | Wed Sep 18 22:53:24 EDT 2002 | davef
Please give us background on your situation, so that we can focus on the specifics, for instance: * This is a bare board problem, correct? Then, this contamination causes what the problems in your process? * What is the type [ie, FR4, CEM1, etc] of
Electronics Forum | Fri Dec 08 14:35:28 EST 2006 | glynnhamer
We currently are building a pcb that has gold fingers, about 36 in a concave V overall shape from .275 on the outside edge fingers tapering down to .197 in the middle of the 2 inch span that plugs into a shelf connector. These fingers are on both sid