Electronics Forum | Wed Sep 29 21:18:28 EDT 1999 | Dreamsniper
| | I finaly get a vacation and decide to go to the forum and low and behold it's hot air verses a small ray of sun.I read every thread and still failed to see any real argument either way? I love rework as an assembler. I hate rework as a shop owner
Electronics Forum | Tue Sep 28 08:27:55 EDT 1999 | Earl Moon
| if anyone has used or has one of these bga rework stations please give me your opinion on them. I am planning on using the sytem for not only rework but also low volume prototype production for hand built 1 or 2 qty pcb's, so ease of use is impor
Electronics Forum | Wed Sep 29 12:51:55 EDT 1999 | Bob Barr
Never heard of the DRS-22C. I have had a DRS-22 for several years now. Purchased it when we started doing BGA's. The operators like it - good optics (split view), built like a tank, X-Y table easy to manipulate for alignment. I like it because I ca
Electronics Forum | Thu Sep 23 06:10:52 EDT 1999 | Wolfgang Busko
| | | Question for you SMT guru's out there. | | | | | | What is the best way to support boards on Fuji's CP6 machine's x-y table...particularly for 2nd side SMT where the support side already has parts... I am toying around with the following meth
Electronics Forum | Fri Sep 24 06:38:15 EDT 1999 | pgarsoe
| | Hi All, | | | | We have 19 Siemens machine running here and lately I was assigned to come out with a proposal on the wrong part issue on Siemens Machines. All of our machines are equip with siemens part verification in which there the part barco
Electronics Forum | Fri Sep 17 23:59:40 EDT 1999 | JAX
| | | HI everyone, | | | | | | We are using a Siemens ap-25 screen printer, in the past we have not had any problems with adhesive placement until a couple of weeks ago. It seems the x axis has decided that it should be set somewhere between .00
Electronics Forum | Fri Sep 17 03:55:45 EDT 1999 | Brian
| We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a reco
Electronics Forum | Sat Sep 18 13:05:57 EDT 1999 | Brian
| | | | | | Dave, I'll respond by paragraph: | | | | | | | Brian: | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like habanero slath
Electronics Forum | Sat Sep 18 14:37:00 EDT 1999 | Earl Moon
| | | | | | | | | Dave, I'll respond by paragraph: | | | | | | | | | Brian: | | | | | | | | I like Ag2 also. I prefer it over both 63/37 and 60/40, if the price is not a factor. Yes, gold rips through eutectic and near-eutectic solders like
Electronics Forum | Thu Sep 16 02:48:48 EDT 1999 | Brian
| Is feasible to have an electronic manufacturing company near the beach? How affect the corrosion the electronic components? | I guess it depends what you mean by 'near'. Will the building be a custom design or an existing one? What kind of product