Electronics Forum | Thu Jul 07 10:56:49 EDT 2005 | Charls R
Hello friends, We have wave soldering m/c Stainless Steel Solder tank. We have in process to chengeover to Lead Free Tank. As for as my concern Titanium coating to tank is one solution. Is there any otehr metal alloy tank is available? if yes what s
Electronics Forum | Tue May 08 22:34:53 EDT 2007 | davef
Do you mean "how to solve or reduce this defect at wave soldering process" while continuing to use-up my SACX solder? If so, try: * Smaller solder volumes lower shrinkage hole / hot tears [Higher hole diameter versus pin diameter helps in reducing v
Electronics Forum | Wed Jun 15 02:09:50 EDT 2016 | twhoo
Anybody see this kind of reject. The thru hole ring turns black (certain area) after wave soldering. The affected area cannot be soldered. Manual touh up is also not possible. Anybody what is the cause of this? Any lab test to prove what is the ite
Electronics Forum | Mon Feb 28 10:54:08 EST 2005 | lyrtech
I have another question: Does the slope of the conveyor is an important parameter in the solder joint quality? What is the standard in degree? Does that parameter can resolve my problem of partial fulling hole (between 50 and 75%)?
Electronics Forum | Mon Feb 28 12:50:20 EST 2005 | russ
If you don't have Plated through holes you will not get any hole fill! There is nothing for the solder to wet to. Problem solved? Russ
Electronics Forum | Fri Jul 04 06:49:41 EDT 2014 | padawanlinuxero
Hi We had the same problem but it turns out the problem is with the supplier we use a water base flux too, supplier change the solder mask and it work. cheers!
Electronics Forum | Fri Feb 22 18:36:36 EST 2013 | austinpeterman
Has anyone experienced bridging on topside (solder destination side) surface mount devices after wave soldering? We x-rayed 100% of the placements after smt re-flow with no issues. When the same placements were x-rayed after the tht wave solder pro
Electronics Forum | Fri Oct 17 15:23:28 EDT 2014 | davef
First, don't exceed the maximum temperature of the battery, say 85*C [I don't know your specifics] Second, don't short the terminals of the battery. Third, the best way to wave solder a battery is: * Insert an insulating tab between the battery an
Electronics Forum | Wed Aug 06 04:11:56 EDT 2008 | chrispy1963
GR@ICS, can you be more specific about your up in the Ersa machine please? Nozzle size, pump rate (%), and is your machine equipped with monitors on the solder pots? We have the same machine it sounds like, however we run Pb-Free in both pots. I
Electronics Forum | Thu Apr 26 09:03:35 EDT 2007 | ck_the_flip
3d is good for initial verification that your screen printer and stencil is producing the desired paste height. 2D verification is more than sufficient during regular production. That being said, your best bet for a 3D machine is to go cheap - buy