Electronics Forum | Thu Jan 20 12:32:40 EST 2000 | Dave F
Hey Dreamguy: On stand-offs: * "Sugar" stand-offs look nice, after washing (if you wash, as Chad said), but we find them kinda fragile. The only people that can install 'em without bustin' more than they install are the "skill people" that we don
Electronics Forum | Tue Dec 14 09:32:59 EST 2004 | patrickbruneel
Hi Paul, One thing I can tell you for sure "lead free" is not going to solve your problem, because spectrum analysis have shown that dendrites at there final stage always consists of pure tin. The higher the tin content the higher the risk for dead
Electronics Forum | Fri Feb 18 09:41:44 EST 2000 | James Lewis
Has anyone seen or put together a good collection of proper handling procedures for components and PCB's? I realize a lot of it is no-brainer stuff, but I need some depth for a training class we are putting together. This would include ESD, Moisture
Electronics Forum | Wed Oct 04 14:46:46 EDT 2000 | Kal. Chak.
Hi folks, What are the differences between Epoxy resin(ER)conformal coating and adhesive stacking/bonding material? My PSA/PRA (Post solder/reflow assembly)bracket assembly process got some ER adhesive encroachment on pads/solderjoints. I have chec
Electronics Forum | Fri Feb 18 09:41:44 EST 2000 | James Lewis
Has anyone seen or put together a good collection of proper handling procedures for components and PCB's? I realize a lot of it is no-brainer stuff, but I need some depth for a training class we are putting together. This would include ESD, Moisture
Electronics Forum | Fri Jul 20 17:09:10 EDT 2001 | davef
Circuits Assembly magazine 09/99 "Defluxing with Ultrasonics" by Les Hymes. [There's more but I can't find it right now. I'll add to this as I find the junk, er very nice stuff.] J-STD-001C states that its OK to use ultrasonics for cleaning so lon
Electronics Forum | Sun Jun 07 06:05:37 EDT 1998 | Bob Willis
| Can anyone tell me if there is a reference for smt component height specs on the bottom side of a board, which will also go through wave soldering. A current design I am reviewing has tant caps(7343) and a crystal on the back side. Should I only b
Electronics Forum | Thu Apr 02 11:19:41 EST 1998 | Justin Medernach
| I am looking for footprint details on a SM crystal. | Package type - Golledge GSX49-4. | Solder method - refolw Mark, Check with the good folks at IPC for land design. The spec should be IPC-SM-782. Also, see http://www.ITM-SMT.com. It's Phil Za
Electronics Forum | Wed Sep 05 14:53:45 EDT 2001 | Jeff Meier
We have customers that are requiring no flux residue left on boards after soldering of non-water washable parts. We currently use Multicore Crystal 502 No-Clean to solder parts that are not washable. Has anyone come up with a good way to remove this
Electronics Forum | Tue Aug 06 17:14:33 EDT 2002 | melo_guy
I thought this would be a good place to post to get input from the "trenches" as to what is going to be the next consumer fad? It seems like the market is in need of something new to instigate future consumption. I work for an electronic component