Electronics Forum | Fri Jun 18 20:09:52 EDT 1999 | Dean
| Has there anyone bold enough to try this in their shops? My cubemate just got through telling me that at his last shop, they had bare copper boards (no HASL, no OSP, no nothing), with minimal solderability problems. | yes, 8 years ago I developed
Electronics Forum | Mon Apr 26 17:45:26 EDT 1999 | Earl Moon
| | | Earl said, in essence: | | | | | | | Justin is absolutely right ... | | | | | | | | Again, Entek is not much more than a flux coating ... | | | | | | | | Metallic coatings protect best, as we all know - especially those electroplated. Those
Electronics Forum | Thu Nov 19 11:06:40 EST 1998 | Earl Moon
| We have some PCB�s in our warehouse in Manaus - Brazil. They are stored for more than 2 years , in a condition of 25 degrees centigrades and a humidity ranging from 60% to 90%. | Do these conditions cause the PCB�s to deteriorate over time? If so ,
Electronics Forum | Wed Jul 29 20:53:44 EDT 1998 | Dave F
| Howdy all- | Does anybody have any experience with solid solder deposits as an alternative | to paste deposits? I have heard many good things, but do board fabricators have | the technology to do this? Where can I get more information on ho
Electronics Forum | Fri Jul 10 09:56:11 EDT 1998 | Justin Medernach
| I am looking for some guidelines on evaluating solder paste. I am specifically interested in No-Clean Pastes, as they are a completely new ball game when it comes to slump, tack time, stencil life, tack time, etc. | Thanks for any and all help give
Electronics Forum | Mon Nov 19 20:15:39 EST 2001 | davef
Now, that is one thickass board!!! The rant first: If our �board supplier changed our board surface finish on� anything without our approval, the board supplier would be an �X�. Life has enough surprises. And of all the flat finishes available, h
Electronics Forum | Tue Jul 15 16:12:23 EDT 2008 | boardhouse
Hi Armynski, I sell for an offshore board house, yes, it is common for offshore board shops to fill vias. The bubble is caused by air entrampment within the hole it self, when heat is applied during Hot air and the via is covered on both sides the e
Electronics Forum | Thu Jul 05 19:39:19 EDT 2001 | davef
I had forgotten that it was you that was on the Sipad adventure. [But then again, who can keep track of yer aliases? ;-)] You just go from one adventure to the next. Expanding On Dave�s Hi-Test Flux Method Theory � PASTE: Yes, contact your favorit
Electronics Forum | Wed Jan 05 11:11:09 EST 2000 | Dave F
Hey Pat: My responses are: 1. Does anyone have experience with the shelf life on immersion white tin? If so, how long can the boards be stored without adversely affecting solderability. I've heard one year. No, we don�t, because we turn boards fa
Electronics Forum | Fri Jan 11 17:14:13 EST 2002 | davef
We have one product with electroless nickel, immersion silver solderability protection. We do not purport to be experts, but like many things, have seemingly boundless opinions. Side note: There are a least three different [maybe five] imm silver