Electronics Forum | Mon Dec 13 21:11:53 EST 1999 | Curtis T.
Steve, I have done countless board profiling and oven reflow profiles. Here are the critical factors on you need to address. What is your board surface finish, if it is something like an OSP it will need a good amount of an active (aqueous) flux to
Electronics Forum | Thu Oct 14 18:02:31 EDT 1999 | JohnW
Bryan, 0402's tombstonning isn't that uncommon and usually the 1st reaction is alway's the pad size aint right. If you've followed the IPC guidline's normally you should be fine but I'd double check the component supplier's spec's as well. brian's p
Electronics Forum | Mon Apr 19 17:33:17 EDT 1999 | Tuffty
25 PPM)! | | | | 1. Is there a better process to solder the leads of QFP's with lifted "minute" lifted leads still having a realiable solder joints? | | | | 2. Or has anybody tried modifying solder pads and use thicker solder paste deposit to compe
Electronics Forum | Thu Mar 25 02:22:32 EST 1999 | P.L. Sorenson - Technical Consultant
| | | Your problem may be related to silver migration (leaching) into the solder. I had what seems to be a similar problem. The solution was using solder with 2% silver content. See these pages for a bit more information: | | | | http://www.ferr
Electronics Forum | Thu Mar 25 13:53:28 EST 1999 | Bob Willis
| | | Your problem may be related to silver migration (leaching) into the solder. I had what seems to be a similar problem. The solution was using solder with 2% silver content. See these pages for a bit more information: | | | | http://www.ferr
Electronics Forum | Fri Mar 12 11:59:50 EST 1999 | Ray Morford
AVX and a few other companies make these chip transient voltage suppressors (TVS) parts that are a real *PAIN* to use. According to AVX: "Due to the semiconducting nature of the doped Zinc Oxide (ZnO) ceramic material, SMT TransGuards are no
Electronics Forum | Mon May 18 20:57:06 EDT 1998 | Earl Moon
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get in
Electronics Forum | Mon May 18 22:54:04 EDT 1998 | Dave F
.025" pitch so the only problem we run into is too much HASL on the adhesive side causing improper glue dispense. | | As Earl keeps saying HASL thickness is hard to impossible to control. I think we need to look hard at OSP's again but then you get
Electronics Forum | Fri May 15 21:59:42 EDT 1998 | Earl Moon
| Hi, | There has been a lot of disputes in our company | about changing present HASL to another Finishing | which can provide more flatter pad surface in fine | pitch applications. ( perhaps Ni/Au, OSP ) | The target is to reduce solder defects, t
Electronics Forum | Tue Apr 14 09:38:07 EDT 1998 | Earl Moon
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X