Electronics Forum | Tue Jul 30 14:07:01 EDT 2002 | cnoonan
Slim KIC would be my choice out of these two vendors. I have worked with several different makes and models and I would say DataPaq was my favorite. But it all depends on your needs and budget. They can all get the job done. Good luck with your
Electronics Forum | Fri Aug 09 10:03:43 EDT 2002 | Eliud Rivera
I was once an SMT Engineer but now I'm in charge of the calibration and maintenance of all the plant equipment. What I use is a program called Maintenance Log Pro from http://www.hginet.com/ You could request a demo and see how it works. At this
Electronics Forum | Wed Jul 31 12:47:34 EDT 2002 | mzaboogie
Hi Patrick, We are using AIM 266-3. The topside preheat temp is approx 100 degrees C although we have played with that number both up and down. Raising the temp leaves a white residue, lowering the temp (below about 90 degrees) and the solder balls
Electronics Forum | Mon Aug 05 09:06:29 EDT 2002 | Adam
I'd like to ask for feedback on monitoring the reflow oven using a copper plate.Are there any articles relating to the above, in the sense of what size the copper plate should be, how many thermocouples should be attached, the frequency of measure me
Electronics Forum | Wed Aug 14 11:41:02 EDT 2002 | lloyd
uuumm, we have four lines in this particular part of the factory all used for curing glue only. our other reflow lines are in another section of the factory with seperate ducts. These lines are however next door to the solder baths.....I will have to
Electronics Forum | Mon Aug 19 09:42:56 EDT 2002 | blnorman
I agree with analysis. You'll never accurately find the source until you determine exactly what the "goo" is. We have this problem, but like previous posters, the goo is flux residue. We do use the ovens for both reflow and adhesive cure. The adh
Electronics Forum | Tue Aug 13 15:55:10 EDT 2002 | jseagle
I am looking for advice on purchasing a used '98-'00 Electrovert Electra wave soldering machine. Are there any specific parts of the machine I should closely inspect? Any specific options I should make sure it has? I will need it to have a spray f
Electronics Forum | Wed Aug 14 16:34:46 EDT 2002 | ksfacinelli
I have a PCB laminate that is 1 1/2 years old and showing signs of poor solderability. The NC flux I am using will not breakdown the oxides. During hand soldering the pads do not take solder. I am trying alternative fluxes and have seen an improve
Electronics Forum | Mon Aug 19 04:57:17 EDT 2002 | surachai
SIPAD solid solder deposit and glue dots is an > excellent solution. > > http://www.sipad.com > > Matt > Kehoe SIPAD Systems Inc Thank you for your information , but I would like to know the information of normal process like a flip process bu
Electronics Forum | Fri Aug 16 06:52:00 EDT 2002 | Bach Huss
We are using the MVT as our AOI Machine. Some how after the reflow (in Testing) we still find defects. We think missing part should not happen once we have the MVT. However there are still escapee from the MVT (0.5 %). We are actually planning to h